Abstract:In this study, the in-situ ZrB 2 /Al-Si5Cu3 aluminum alloy composites were fabricated through the salt-melt reaction route with different weight fractions of ZrB 2 reinforcements, i.e., 2.5%, 5%, and 7.5%. The composites were tested for their density, hardness, tensile strength, flexural strength, impact strength, and wear properties. The influence of reinforcement on the properties was studied concerning the wt.% of reinforcement. The increase in density of composites compared to the matrix material confirms the formation of the in-situ reinforcement phase. The microstructure showed a desirable distribution of reinforced particles over the matrix at all weight fractions of the reinforcements in the composites. The ZrB 2 particles formed in the matrix have particle sizes in the range from 255 nm to 955 nm and the grain size has been reduced from 242 microns to 110 microns as the result of particle-induced solidification. The hardness of the composites containing ZrB 2 reinforcements of 2.5, 5, and 7.5 wt.% showed improvement by 8%, 17.5%, and 34% respectively compared to the parent alloy. There is an improvement in the tensile strength and elongation for the wt.% of ZrB 2 up to 5 wt.%, from 115 MPa to 183 MPa, after which, there was a drop in the tensile strength. The detailed analysis of tensile fractography shows that the agglomerated ZrB 2 reinforced particles at higher weight fractions lead to a decrease in strength. The results of flexural strength also affirm the strength of 5 wt.% ZrB 2 /Al-Si5Cu3 increased from the matrix material's flexural strength of 337 MPa to 672 MPa. The wear study shows that the composite with 7.5 wt.% ZrB 2 possesses a higher wear resistance. However, the impact strength did not show any differences in the weight % of reinforcement.

Serrated flow and ZrB2 nanoparticle agglomerations of in-situ AA6061 alloy matrix composites

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

In situ (Al3Zrp+Al2O3np)/2024Al metal matrix composite with controlled reinforcement architecture fabricated by reaction hot pressing

Effects of ZrB2 Nanoparticles on the Microstructures and Tensile Properties of a Hot Extruded In Situ AA6111 Composite

Microstructures and mechanical properties of the in-situ formed nanocomposites of (ZrB2 + Al2O3) and AA7055 alloy

Microstructure evolution and mechanical properties of in-situ ZrB2/Al7085 nanocomposites during hot rolling deformation

Effect of nanoparticle fraction on Portevin-Le Chatelier effect of ZrB2 nanoparticle-reinforced AA6xxx composites

Microstructures, mechanical and strain hardening properties of squeezed 6016Al matrix composites synthesized under electromagnetic field

Enhanced Combination of Strength and Ductility in Ultrafine-Grained Aluminum Composites Reinforced with High Content Intragranular Nanoparticles

Microstructure and mechanical properties of friction stir welding joint of in-situ ZrB2/AA7085 composites

Effect of in-situ ZrB 2 nanoparticles on microstructure and mechanical properties of friction stir welding joints in 7N01 matrix composites

Effects of ZrO2 nanoparticles on the microstructure and mechanical properties of ZrO2/AlSi10Mg composites manufactured by laser powder bed fusion

Strengthening Behaviors and Strength Differential Effect of Nano-Zrb2-particle/aa6xxx Alloy Composites

Microstructure and mechanical properties of laser beam welding joint of in-situ (ZrB2+Al2O3)/AA7N01 nanocomposites

Investigation on high-temperature creep property and mechanism of AA6111 matrix composites reinforced by in-situ ZrB 2 nanoparticles

Microstructural Evolution & Mechanical Properties of ZrO2/GNP and B4C/GNP reinforced AA6061 Friction Stir Processed Surface Composites - A Comparative study

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

Mechanical and Wear Behavior of Al-Si5Cu3/ZrB2 In-Situ Reinforced Metal Matrix Composite

Effects of in-situ ZrB 2 nanoparticles and scandium on microstructure and mechanical property of 7N01 aluminum alloy

Effects of Yittria Stabilised ZrO2 Nanoparticles on the Strengthening Mechanisms in AlSi10Mg Fabricated by LPBF

High Strain Rate Superplasticity of in situ Al 3 Zr/6063Al Composites