Microscopic phase-field study on L12 interface properties of Ni75Al18Cr7 superalloy

Hailei Hu,Weiping Dong,Mingyi Zhang,Mengjia Li,Zheng Chen

DOI: https://doi.org/10.1016/j.jallcom.2021.162420

IF: 6.2

2022-02-01

Journal of Alloys and Compounds

Abstract:In this study, the solidification and precipitation process of Ni75Al18Cr7 superalloy was investigated based on the microscopic phase-field method. The simulation results were validated by using the experimental results. There were three types of ordered interfaces between L12 phase, namely (200)L//(200)L·½[001]L, (200)L//(200)L and (100)L//(200)L·½[001]L, which were studied by plotting the microstructural characteristics of Ni75Al18Cr7 superalloy and the distribution of atomic occupation probability and evolution of atomic occupation probability on both sides of the interface between L12 phases. The simulation results show that the former two interfaces could migrate with the precipitation evolution process, while the latter ordered interface (100)L//(200)L·½[001]L could not migrate. The interface migration was caused by the migration and exchange of Ni/Al atoms at the ordered interface. The atomic concentration in the ordered interface before and after migration was almost constant, i.e., the segregation and dilution of each atom was almost constant. The experimental results show that the L12 phase structure grew gradually with the increase in heat treatment time, which is consistent with the simulation results of microscopic phase-field method. Moreover, the volume fraction of L12 phase calculated by the phase-field method was almost the same as that obtained by X-ray diffraction (XRD) experiments, which indicates the feasibility of using microscopic phase-field method to guide the optimization design of alloy.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering