Boosting fill factor and open-circuit voltage of carbon-based perovskite solar cells with graphene co-doped P3HT/NiOx hole-transporting bilayer
Yuhao Song,Bingjie Xu,Yingying Deng,Miaosen Yao,Junjie Tong,Qichao Wang,Wanlong Wang,Gentian Yue,Weifeng Zhang,Chen Dong,Furui Tan
DOI: https://doi.org/10.1039/d3tc04665f
IF: 6.4
2024-04-07
Journal of Materials Chemistry C
Abstract:Low-cost and stable carbon-based perovskite solar cells (C-PSCs) have been regarded as the most competitive device architecture for PSC commercialization. However, due to the large interfacial resistance and energy-level mismatch between the carbon-electrode and perovskite, C-PSCs have been suffering from low fill factor (FF) and open-circuit voltage (Voc) deficit, limiting their efficiency. Here, a low-temperature, solution-processed P3HT/NiOx organic/inorganic hybrid bilayer with graphene (G) as co-dopant is developed as hole-transporting layers (HTLs) for C-PSCs. The optimal G-P3HT/G-NiOx bilayer HTLs not only provide the well-matched cascade band alignments that facilitate the charge separation and extraction, and reduce the recombination loss at the perovskite/carbon-electrode interface, but also their G co-dopants build the carrier highways within NiOx and P3HT matrix, accelerating the charge transport and thus reducing FF loss. As a result, a Voc improvement of 100 mV, an FF of up to 79.2 %, and a champion power conversion efficiency (PCE) of 19.1 % for C-PSCs are achieved. More importantly, the unencapsulated devices with G-P3HT/G-NiOx bilayer HTLs remain 88 % of their initial PCE in ambient air for 2,500 h and 91 % - upon continuous heating at 85 °C for 637 h, along with 77% of the initial efficiency retained over 12,000 min of operation at maximum power point. This work provides valuable experience for designing bilayer HTLs toward highly efficient and stable C-PSCs.
materials science, multidisciplinary,physics, applied