Fully printed flexible perovskite solar modules with improved energy alignment by tin oxide surface modification

Lirong Dong,Shudi Qiu,Jose Garcia Cerrillo,Michael Wagner,Olga Kasian,Sarmad Feroze,Dongju Jang,Chaohui Li,Vincent M. Le Corre,Kaicheng Zhang,Heiko Peisert,Felix U Kosasih,Charline Arrive,Tian Du,Fu Yang,Christoph J. Brabec,Hans-Joachim Egelhaaf
2024-06-05
Abstract:Fully printed flexible perovskite solar cells (f-PSCs) show great potential for the commercialization of perovskite photovoltaics owing to their compatibility with high-throughput roll-to-roll (R2R) production. However, the challenge remains in the deficiency in controlling interfacial recombination losses of the functional layer, causing remarkable loss of power conversion efficiency (PCE) in industrial production. Here, a fullerene-substituted alkylphosphonic acid dipole layer is introduced between the R2R-printed tin oxide electron transport layer and the perovskite active layer to reduce the energetic barrier and to suppress surface recombination at the buried interface. The resulting f-PSCs exhibit a PCE of 17.0% with negligible hysteresis, retain 95% of their initial PCE over 3000 bending cycles and achieve a T95 lifetime of 1200 h under 1 sun and 65 degreeC in nitrogen atmosphere. Moreover, the fully printed flexible perovskite solar mini-modules (f-PSMs) with a 20.25 cm2 aperture area achieve a PCE of 11.6%. The encapsulated f-PSMs retain 90% of their initial PCE after 500 h damp-heat testing at 65 degreeC and 85% relative humidity (ISOS-D3). This work marks an important progress toward the realization of efficient and stable flexible perovskite photovoltaics for commercialization.
Materials Science,Applied Physics
What problem does this paper attempt to address?
This paper mainly addresses the problem of the decrease in power conversion efficiency (PCE) in flexible perovskite solar cells (f-PSCs) due to insufficient control of interface recombination losses. The research team introduced a fullerene substituted alkylphosphonic acid dipole layer between the tin oxide electron transport layer and the perovskite active layer printed by roll-to-roll (R2R) printing, which lowered the energy level barrier and suppressed interface recombination. This method improved the PCE of f-PSCs to 17.0% and maintained 95% of the initial efficiency after 3000 bending cycles, with good stability in a nitrogen environment. In addition, they also fabricated f-PSMs with an area of 20.25 square centimeters, achieving 11.6% PCE and maintaining 90% of the initial efficiency after humidity testing. This work is of great significance for the commercialization of efficient and stable flexible perovskite photovoltaics.