Flexible perovskite solar cells with simultaneously improved efficiency, operational stability, and mechanical reliability

Qingshun Dong,Min Chen,Yuhang Liu,Felix T. Eickemeyer,Weidong Zhao,Zhenghong Dai,Yanfeng Yin,Chen Jiang,Jiangshan Feng,Shengye Jin,Shengzhong Liu,M. Zakeeruddin,Michael Grätzel,Nitin P. Padture,Yantao Shi,Shengzhong (Frank) Liu,Shaik M. Zakeeruddin

DOI: https://doi.org/10.1016/j.joule.2021.04.014

IF: 46.048

2021-06-01

Joule

Abstract:Although great progress is being made toward improving the power conversion efficiency (PCE) and the operational stability of perovskite solar cells (PSCs), little attention is being paid to their mechanical reliability, which is particularly important for flexible PSCs (f-PCSs). Here, we have grown low-dimensional (LD) metal-halide perovskite (MHP) thin capping layer over the 3D MHP light-absorber thin film in f-PSCs <em>in situ</em> to improve their mechanical reliability. This resulted in f-PSCs with unprecedented, simultaneous improvements in PCE (21.0%), operational stability (T90, retention of 90% of the initial PCE, &gt;800 h), and bending durability (T80 = 20,000 tension-only bending cycles). These synergistic virtuous effects are attributed to the LD MHP capping layer enhancing photocarriers extraction, providing protection against the environment, and "sealing" surface flaws on the 3D MHP thin film. The latter reduces the propensity for cracking in bending, which results in improved environmental stability and bending durability.

materials science, multidisciplinary,chemistry, physical,energy & fuels

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the comprehensive performance of flexible perovskite solar cells (f - PSCs), specifically including:

1. **Improve power conversion efficiency (PCE)**: Optimize materials and structural design to enhance the energy conversion efficiency of the cell.
2. **Enhance operational stability**: Ensure the stable performance of the cell during long - term operation and reduce performance degradation.
3. **Improve mechanical reliability**: Improve the durability of the cell under mechanical stresses such as bending and stretching, and extend its service life.

To achieve these goals, the author used 3 - CBAI (3 - chlorobenzylammonium iodide) to react with PbI₂ to in - situ grow a low - dimensional (LD) MHP capping layer on the surface of the 3D metal halide perovskite (MHP) thin film. This method not only improves the PCE but also significantly enhances the operational stability and mechanical reliability of the cell. Specifically:

- **PCE**: The PCE of the champion device reached 21.0%.
- **Operational stability**: T90 (retaining 90% of the initial PCE) exceeded 800 hours.
- **Bending durability**: T80 (retaining 80% of the initial PCE) reached 20,000 one - way bending cycles.

These improvements are attributed to the positive effects of the LD MHP capping layer in the following aspects:

- **Enhance photocarrier extraction**: The LD MHP capping layer improves the extraction efficiency of photocarriers.
- **Environmental protection**: The capping layer provides protection against environmental factors (such as oxygen and water), reducing the impact of the environment on cell performance.
- **Seal surface defects**: The capping layer "seals" the defects on the surface of the 3D MHP thin film, reducing the generation of cracks, thereby improving mechanical reliability and bending durability.

Through these synergetic effects, the author has successfully demonstrated a flexible perovskite solar cell with an unprecedented improvement in comprehensive performance.