Abstract:Significant efforts have been made to improve concrete mix design for shrinkage reduction and crack control, including reduction of cement content and selection of cement type with less heat of hydration, maximizing aggregate contents, and introduction of discrete fibers in concrete to increase internal restraint. Although high-performance concrete (HPC) mixes including fibers [e.g., steel fibers, polypropylene fibers, or polyvinyl alcohol (PVA) fibers] have reduced the level of shrinkage cracking, they have not eliminated it. Thus, understanding the level of tensile strain the fibers take in the concrete could provide valuable information to aid engineers to make an informed decision on the need for fibers in tension demand in the concrete and determine the appropriate fiber detailing and concrete mix additives. As such, this study aimed to explore a multiscale, hierarchical fiber gradation through a combination of nanoscale nanofabrillated cellulose (NFC) with microscale sisal fibers and macroscale steel fibers in concrete to mitigate the causes of concrete shrinkage cracking at an early age. A total of 22 mixtures were designed and tested. The results show that nanofabrillated cellulose, sisal fiber, and steel fiber can play an excellent synergistic effect to inhibit the early-age shrinkage of concrete. The test data reveal that, when steel fiber is partially replaced by sisal fiber, the early shrinkage of steel fiber concrete is significantly reduced by 26.91% at maximum. Meanwhile, when the NFC content reached 0.15%, the 7-day shrinkage value of concrete reinforced by steel fiber, sisal fiber, and NFC was the lowest, and the shrinkage strain value decreased by 25.03% compared with N0. Compared with the experimental group in which sisal fiber partially replaced steel fiber, the 7-day shrinkage value of the experimental group in which sisal fiber mixed with NFC, sisal fiber mixed with NFC and steel fiber decreased to a certain extent, among which SF1.1FF0.4NFC0.15 showed the best shrinkage inhibition performance, and the shrinkage strain value decreased by 82.56% and 45.39% compared with N0 and SF1.1FF0.4, respectively.

Evaluation of the Addition of Polypropylene (PP) Fibers in Self-compacting Concrete (SCC) to Control Cracking and Plastic Shrinkage Between Different Methods

Shrinkage and Creep of Sustainable Self-Compacting Concrete with Recycled Concrete Aggregates, Fly Ash, Slag, and Silica Fume

Experimental study on effects of polypropylene fiber on early-age shrinkage in concrete

Strength and Early Crack Resistance Experiment of Polypropylene Fiber Reinforced Concrete with Silicon Powder

The effect of polypropylene fibres on the compressive strength, impact and heat resistance of self-compacting concrete

Influence of Superabsorbent Polymer in Self-Compacting Mortar

Effect of the Combination of Superabsorbent Polymers for Autogenous Shrinkage Control with Steel Fibers of High-Performance Concrete under Uniaxial Tension Using DIC

Influence of Polypropylene and Steel Fibers on the Performance and Crack Repair of Self-Compacting Concrete

Performance of Manufactured and Recycled Steel Fibres in Restraining Concrete Plastic Shrinkage Cracks

Early-age autogenous shrinkage, tensile creep, and restrained cracking behavior of ultra-high-performance concrete incorporating polypropylene fibers

Effects on the Properties of Self-Compacting Cement Paste (PAA) with the Addition of Superabsorbent Polymer

Optimisation of polypropylene and steel fibres for the enhancement of mechanical properties of fibre-reinforced concrete

Ultra-high performance of eco-friendly self-compacting concrete incorporated cement Kiln dust with/without waste plastic and polypropylene fiber

Performance evaluation of indented macro synthetic polypropylene fibers in high strength self-compacting concrete (SCC)

Evaluation of performance of hybrid fiber-reinforced self-compacting concrete using non-destructive testing techniques

Influence of an over calcined calcium oxide-based shrinkage-compensating admixture on some properties of a self-compacting concrete

Effectiveness Assessment of Superplasticizer Admixtures: Case of Self-compacting Concrete Reinforced with Fine Mineral Fillers

Multiscale Hierarchical Fiber Gradations in Concrete to Reduce Early-Age Shrinkage Cracking Potential

Early-age autogenous shrinkage and tensile creep of concrete reinforced with polypropylene macro fiber

Study on early-age cracking resistance of multi-scale polypropylene fiber reinforced concrete in restrained ring tests

Test Method for Studying the Shrinkage Effect under Controlled Environmental Conditions for Concrete Reinforced with Coconut Fibres