Abstract:In the process of long-term service of concrete, cracks are inevitable, especially in the state of tension and compression, the crack expansion speed is accelerating, which seriously affects the service performance of concrete, and even causes major disasters. While polypropylene fiber has remarkable cracking resistance, there is a lack of theoretical analysis on crack initiation and path expansion of concrete cracks with existing cracks during the compression process. In order to analyze the inhibitory effect of fiber on the propagation of pre-existing cracks, we performed uniaxial compression tests on concrete prisms containing pre-existing cracks. Acoustic emission technology was used to monitor each test group and obtain relevant data on the cracking process of the specimens. GDEM software was used to simulate typical test conditions, and the results were compared with the test results to further explain the mechanism of crack propagation and fiber suppression. The results show that: (1) fiber can inhibit the initiation and propagation of tension wing cracks at the existing crack tip. The higher the fiber content, the shorter the symmetrical wing cracks become. (2) With the increase of fiber content (0 ∼ 4 kg/m 3 ), the failure mode of polypropylene fiber-reinforced concrete prismatic specimens changes from tensile failure to tensile-shear failure, and finally shear failure. (3) The crack initiation stress and peak strength of prismatic specimens first increase and then decrease with the increase of fiber content. (4) The increase of fiber content delays the crack initiation time, prolongs the time to the disappearance of the peak of the acoustic emission signal, and prolongs the total time of the failure process.

Study on early-age cracking resistance of multi-scale polypropylene fiber reinforced concrete in restrained ring tests

Experimental study on effects of polypropylene fiber on early-age shrinkage in concrete

Strength and Early Crack Resistance Experiment of Polypropylene Fiber Reinforced Concrete with Silicon Powder

Analytical Prediction and Experimental Research on Shrinkage Cracking of Restrained Early-Age Concrete

Early-age autogenous shrinkage, tensile creep, and restrained cracking behavior of ultra-high-performance concrete incorporating polypropylene fibers

Early-age autogenous shrinkage and tensile creep of concrete reinforced with polypropylene macro fiber

Study on the influence mechanism of polypropylene fiber on crack propagation of concrete with existing cracks under uniaxial compression

Flexural fatigue performance and damage evolution analysis of multiscale polypropylene fiber‐reinforced concrete

Research on the Stressed Performance of Polypropylene Fibrous Concrete Ditch

Investigation on cracking resistance mechanism of basalt-polypropylene fiber reinforced concrete based on SEM test

Microscopic, physical and mechanical analysis of polypropylene fiber reinforced concrete

Experimental study on the axial tensile properties of polypropylene fiber reinforced concrete

Investigation on multi-cracks initiation and propagation of fiber reinforced concrete in restrained shrinkage ring tests

Experimental Investigation on the Mechanical Properties of Polypropylene Hybrid Fiber-Reinforced Roller-Compacted Concrete Pavements

Experimental Study on Cracking Property of Self-Compacting Concrete

A Study of Energy Dissipation of Polypropylene Fiber Reinforced Recycled Concrete Under Uniaxial Compression

Research on Compressive Impact Dynamic Behavior and Constitutive Model of Polypropylene Fiber Reinforced Concrete

Experimental and numerical study on polypropylene fibers reinforced concrete slabs with corroded reinforcement under monotonic loading

Mechanical properties and failure modes of polypropylene fiber-reinforced foamed concrete subjected to high strain rates and large compressive deformation: effects of fiber content and length

Experimental and Simulation Study of the Fracture Instability Behavior in Polypropylene Fiber-Reinforced Concrete

Review on the Durability of Polypropylene Fibre-Reinforced Concrete