Abstract:Ceramic coatings with aluminum titanuate (Al2TiO5) were prepared on Ti–6Al–4V alloy using pulsed bi-polar Micro-arc Oxidation (MAO). The micromorphology and phase composition of the micro-arc-oxidition ceramic coatings on the titanium alloy were characterized by X-ray powder diffraction (XRD), and scanning electron microscopy (SEM) respectively. The results revealed that the distinct discharge channels and pores on the surface of the micro-arc-oxidition coatings appeared, and these channels were connected in the molten state. The electrolyte concentration was inversely proportional to the coating hardness; additionally, the coating prepared with sodium aluminate and sodium hypophosphite concentrations of 4 g/L and 0.5 g/L, respectively, was the most refined after high-temperature sintering, and it was demonstrated to better prevent oxidation. Increasing the electrolyte concentration coincided with fluctuating coating thermal shock resistance. The thermal shock resistance of the coating respectively prepared with sodium aluminate, and the sodium hypophosphite concentrations of 4 g/L and 0.5 g/L was the highest. Additionally, the high-concentration coatings performed significantly better than the low-concentration coatings. The oxidation resistance of the coating samples was also significantly higher than that of the TC4 titanium alloy substrate. The adhesion strength between the coatings and the substrate with and without the sealing treatment was measured by tensile tests. Then, the high-temperature oxidation performance of the coating samples with and without the sealing treatment was investigated by conducting a high-temperature oxidation experiment at a calcinating temperature of 500 °C. The results indicate that the adhesion strength between the coatings and substrate was high for the as-prepared and sealed micro-arc oxidation samples regardless of whether they were calcined. The high-temperature oxidation mass increase curves for the sealed and unsealed coating samples calcined at 500 °C for 500 h revealed that the high-temperature-oxidation-induced mass increase of the coating samples sealed with a sodium silicate solution was much lower than that of the titanium alloy substrate. Thus, the sealing treatment significantly improved the high-temperature oxidation resistance of the TC4 titanium alloy. Lastly, the high-temperature oxidation behavior at 500 °C was analyzed and discussed.

A Study of Heat Resistance of Aluminized Coatings on Titanium

Surface Characterization of Thermally Oxidized Titanium Alloys

Structure and Properties of Ti-Al Intermetallic Coatings Reinforced with an Aluminum Oxide Filler

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

High-temperature oxidation resistance of ceramic coatings on titanium alloy by micro-arc oxidation in aluminate solution

Effect of Temperature and Rate Treatment Parameters on the Structural Phase State and Properties of Ti2AlNb Titanium Aluminide-Based Alloy

Research Status of Aluminum Base Coating on Titanium Alloy

Corrosion Resistance of Coatings Based on Chromium and Aluminum of Titanium Alloy Ti-6Al-4V

Impact of Heat Treatment on the Microstructure and Properties of Ti–Al Composite Coatings with Formation of a TiAl3 Intermetallic Phase

High emissivity coatings on titanium alloy prepared by micro-arc oxidation for high temperature application

Microstructure, Properties and Mechanism of Formation of Aluminum Diffusion Coatings on Heat-Resistant Stainless Steels

Effect of coating thickness on microstructural and mechanical properties of titanium coated aluminum alloy deposited by vacuum arc melting method

Enhanced Resistance of Ti6Al4V Alloy to High-Temperature Oxidation and Corrosion by Forming Alumina Composite Coating

Research Progress on High-Temperature Oxidation and Corrosion Mechanisms of Aluminide Coatings

Phase Composition of Heat-Resistant Layered Coatings of the Al–Cr–Ni System

Microstructure and high temperature performance of titanium modified aluminide coatings applied on GTD-111 superalloy during the rejuvenation heat treatment

Wear and corrosion resistance of titanium carbo-nitride coated Al-7075 produced through PVD

High-temperature oxidation behavior of plasma-sprayed NiCrAlY/TiO2 and NiCrAlY/Cr2O3/YSZ coatings on titanium alloy

Microstructure and Cyclic Oxidation Behavior of Hot-dip Aluminized Coating on TZM Alloy

High Temperature Protection Properties of TiAlN Coating Prepared by Arc Ion Plating on Surface of Ti6Al4V Titanium Alloy

Thermal durability of aluminum titanate-mullite composites with high thermal shock resistance