Abstract:Isothermal oxidation of microcrystalline Ni–11.5Cr–4.5Co–0.5Al (wt%) superalloy sheet fabricated by electron beam physical vapor deposition (EB-PVD) at 900°C in air was investigated. Mass gain curves were obtained on testing the alloy in dry air. And characterization of the surface morphology and cross-sections was performed on samples isothermally oxidized for different exposure times. Surfaces and cross-sections of the oxidized specimens were studied by scanning electron microscopy (SEM). Phase identification of the oxide scale was performed by glancing angle X-ray diffraction (GAXRD) and energy dispersive X-ray microanalysis (EDX). The experiment results indicated that the oxidation kinetics of microcrystalline Ni–11.5Cr–4.5Co–0.5Al superalloy sheet follows a cubical power law at initial oxidation stage and fourth power law for long oxidation terms. The oxide scales consisted mainly of a mixed oxide at initial oxidation stage and a double-layer scale with an outer NiO oxide layer, and inner mixed oxides exposed for long terms at 900°C. The fine oxide grains could be formed on microcrystalline superalloy surface. Taking the short circuit diffusion through grain boundaries into account, an oxidation kinetic with cubical power law in mixed oxide and fourth power law in single-phase oxide were derived. And the excellent fitting of the present model to the experimental data was obtained. The results suggested that the growing oxide layer of microcrystalline Ni–11.5Cr–4.5Co–0.5Al superalloy sheet, which controlled the ionic transportation, contained mainly mixed oxide at initial oxidation stage and the scale/substrate interface single-phase oxide for long terms.

New sight on the oxide film growth mechanism in a single crystal Ni-based superalloy with a ground surface signature

Structural Evolution of Topologically Closed Packed Phase in a Ni-based Single Crystal Superalloy

A study on the multiple stages of oxidation kinetics in a single crystal nickel-based superalloy

Oxidation behavior of a nickel-based single crystal superalloy at 1100 °C under different oxygen concentration

Film evolution and growth mechanism of a Ni-based superalloy in the two models at the different temperatures

The Effect of Surface Machining on the High-Temperature Oxidation of A Single Crystal Ni-Based Superalloy

Microstructural evolution during exposure in air and oxidation behavior of a nickel-based superalloy

High-temperature oxidation and hot corrosion of Ni-based single crystal superalloy in the incubation stage

On the preferential grain boundary oxidation of a Ni-Co-based superalloy

Structural Evolution of a Ni Alloy Surface During High-Temperature Oxidation

Oxidation Kinetics of Microcrystalline Ni–11.5Cr–4.5Co–0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 900 °C

In Situ Full-Field Measurement of Surface Oxidation on Ni-based Alloy Using High Temperature Scanning Probe Microscopy.

Oxidation-induced recrystallization and damage mechanism of a Ni-based single-crystal superalloy during creep

ISOTHERMAL OXIDATION BEHAVIOR OF A SINGLE CRYSTAL NICKEL-BASED SUPERALLOY

Oxidation behavior of 4774DD1 Ni-based single-crystal superalloy at 980 °C in air

On the Development of a Protective Oxide System in Rare Earth Oxide Coated Nickel Superalloy under Isothermal Oxidation Conditions

Precipitation and growth behavior of γ′ phase in Ni3Al-based superalloy under thermal exposure

Investigation of breakaway oxidation kinetics of nickel-base single crystal superalloys: Modeling and experiments

The high-temperature oxidation behavior and mechanism in a powder metallurgy Ni-based superalloy featuring δ-Nb3Al addition

Isothermal oxidation behavior of micro-regions in multiphase Ni3Al-based superalloys

Inhibiting the Formation of Planar Defects in Grown Alumina Scale on Ni-Al Alloys