Abstract:Nickel based superalloys are widely used in such applications as gas turbine blades due to their excellent mechanical properties at elevated temperatures. Oxidation is one of the life limiting factors at such temperatures since it accelerates failure mechanisms, e.g. fatigue and creep. In this project, oxidation behavior of Ni-3Al-4.8Ti-9.5Co-14Cr (wt.%) superalloy was investigated under various testing conditions. The alloy was investment-cast with preferential crystal growth direction [100]. Isothermal oxidation tests were carried out at 800°C for 150h. Cyclic oxidation tests were then conducted between 100-800°C for 150 one-hour cycles. An additional one-hour cycle was tested to replicate real-life working condition of the alloy, which consisted of heating the samples up to 800°C followed by slow cooling to 400°C. During the testing, samples were periodically taken from the furnace and weighted with an accuracy of 10 -4 g to calculate the weight gain and to analyze the microstructure of formed oxide. Scanning electron microscopy (SEM) combined with energy-dispersive spectroscopy (EDS) and X-ray diffraction were used to study the microstructure of oxidation products. The results reveal that the highest amount of weight gain is obtained in isothermal testing, while the lowest in cyclic. Diffusion of Ti and Ni to the free surface results in the early-stage formation of needle-shaped oxide phases followed by severe oxidation of Cr and Al. The layer of chromium oxide is continuous while aluminum oxide is blocky at the deepest position from the free surface. Cracks form at the interface of carbide particles and gamma phase near the free surface of cyclic oxidation samples due to concentration gradient of Ni and Al. Precipitate-free zone are observed near the free surface of all the samples at the end of the tests, but internal oxidation does not occur significantly in all the samples. It is found that temperature fluctuation increases oxide spallation, which causes crack formation. At the same time, in isothermal testing, dense, crack-free layer of oxide form on the surface of superalloy.

Isothermal oxidation behavior of micro-regions in multiphase Ni3Al-based superalloys

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Microstructural evolution during exposure in air and oxidation behavior of a nickel-based superalloy

ISOTHERMAL OXIDATION BEHAVIOR OF A SINGLE CRYSTAL NICKEL-BASED SUPERALLOY

Oxidation behavior of a nickel-based single crystal superalloy at 1100 °C under different oxygen concentration

Effects of Ni and Cr on the high-temperature oxidation behavior and mechanisms of Co- and CoNi-base superalloys

Cyclic and Isothermal Oxidation Behavior of a Directionally Solidified Ni-Al-Ti-Co-Cr Superalloy

Isothermal Oxidation Resistance of As-cast NiAl and NiAl-(Cr, Mo) Eutectic Alloys at 1000°C

The high-temperature oxidation behavior and mechanism in a powder metallurgy Ni-based superalloy featuring δ-Nb3Al addition

High temperature oxidation behavior of a novel Ni-Cr-W-Al-Ti superalloy

On the preferential grain boundary oxidation of a Ni-Co-based superalloy

Microstructural homogenization and high-temperature cyclic oxidation behavior of a Ni-based superalloy with high-Cr content

Oxidation behavior of 4774DD1 Ni-based single-crystal superalloy at 980 °C in air

Influence of microstructure on the oxidation behaviour of the Ni-based single crystal superalloy AM1 between 850 and 1050 °C in air

High-temperature oxidation and hot corrosion of Ni-based single crystal superalloy in the incubation stage

Diffusion of alloying elements during high temperature oxidation in a low-cost third generation Ni-based single crystal superalloy

Oxidation Behaviour of New Nickel-Base Superalloys with Varying Aluminium: Niobium Ratio

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

Isothermal short‐term oxidation behavior of MAR‐M246 nickel‐based superalloy at 800°C and 1000°C

Oxidation behavior of Ni-based superalloy GH738 in static air between 800 and 1000 °C

Directional coarsening behavior of primary γ′ phase in Ni3Al-based superalloy during aging heat treatment