Inhibiting tribocorrosion damage of Cr/CrxN coatings by multi-layer design

Yixuan Wang,Jingwen Zhang,Yongxin Wang,Chunting Wang,Wuming Guo,Xiaojiang Lu,Yongfeng Sui,Jibing Lan
DOI: https://doi.org/10.1016/j.ceramint.2020.08.196
IF: 5.532
2021-01-01
Ceramics International
Abstract:<p>The two-layer and multi-layer Cr/Cr<sub>x</sub>N coatings were fabricated on 316 L stainless steel (316 L SS) substrates by the arc ion plating technique. The two-layer Cr/Cr<sub>x</sub>N coating was a typical CrN coating with an adhesive Cr layer. And the multi-layer Cr/Cr<sub>x</sub>N coating design was in two dimensions. In the first dimension, the multi-layer Cr/Cr<sub>x</sub>N coating consisted of alternative Cr/CrN layers with the thickness ratio of 1:5; in the second dimension, the alternative Cr<sub>2</sub>N layers with the thickness of 10 nm were inserted in CrN layers. This design was expected to increase transverse interfaces in a smaller scale. The microstructures, mechanical, corrosion and tribocorrosion performances of both Cr/Cr<sub>x</sub>N coatings were systematically investigated. The results showed that the special multi-layer design of Cr/Cr<sub>x</sub>N coatings improved mechanical, anti-corrosion and <em>anti</em>-tribocorrosion performances. Compared with the two-layer Cr/Cr<sub>x</sub>N coating, the reduced tribocorrosion damage of the muti-layer Cr/Cr<sub>x</sub>N coating was closely related to the inhibited synergistic effect between electrochemical corrosion and mechanical wear. In conclusion, the multi-layer Cr/Cr<sub>x</sub>N coating was more suitable to work as the surface protective coating than the two-layer Cr/Cr<sub>x</sub>N coating in seawater.</p>
materials science, ceramics
What problem does this paper attempt to address?