Multilayer architecture design to enhance load-bearing capacity and tribological behavior of CrAlN coatings in seawater

Bin Xia,Shengguo Zhou,Yongxin Wang,Hao Chen,Jingwen Zhang,Bingdong Qi

DOI: https://doi.org/10.1016/j.ceramint.2021.06.165

IF: 5.532

2021-10-01

Ceramics International

Abstract:Steel materials employed in severe conditions including strong corrosion, high load and multi-factor coupling damages can easily cause incredible degradation until failure, and the protective CrN-based coatings should be one of promising candidates to relieve those damages for the steel equipment or components. In present paper, the monolayer CrAlN and multilayer Cr/CrAlN coatings were successfully deposited on steel substrates by multi-arc ion technology, and their microstructure, mechanical, tribological and corrosion performances were systematically investigated. The results show that the special multilayer Cr/CrAlN coating could possess much better load-bearing capacity and wear resistance than that of monolayer CrAlN coating, which was due to the facts that the multilayer architecture can effectively release the internal stress and inhibit the expansion of defects. Particularly, the multilayer interfaces could effectively prevent the aggressive medium in seawater infiltrating into the inside of coating, and thus the multilayer Cr/CrAlN coating could have higher corrosion resistance compared to monolayer CrAlN coating. As a result, this multilayer Cr/CrAlN coating could achieve excellent combined performances, indicating that it has greatly potential application as protective coating in seawater.

materials science, ceramics