Abstract:CePO4 was prepared using the co-precipitation method. Recognizing the bifunctional nature of hetero-polyacid (salt), with both acidic and redox properties, it was modified by using phosphotungstic acid (HPW), and the HPW/CePO4 catalysts were synthesized using the impregnation technique. Various advanced techniques were employed to investigate aspects such as catalytic activity, microstructure, surface properties, and reaction mechanisms. These methods included NH3-SCR, XRD, XPS, SEM, BET, NH3-TPD, H2-TPR, and In-situ DRIFTs. Experimental findings indicated that the HPW-modified CePO4 catalysts exhibited enhanced SCR activity. Among them, the reaction activity window for NO x conversion of the W: Ce 0.05 catalyst was found to be 300∼400 °C, which represented the best activity temperature window. Following the incorporation of HPW, the HPW/CePO4 catalysts demonstrated an increased presence of Brønsted acidic sites, which concurrently led to a significant reduction in SO2 adsorption. The W: Ce 0.05 catalyst possessed the highest ratios of Oα/(Oα+Oβ+Oγ) and Ce4+/(Ce3++Ce4+). These ratios effectively regulated the sequestration and release of reactive oxygen species, thereby enhancing the activation of NH3. Consequently, this promoted the catalyst's low-temperature NH3-SCR reactivity. Lastly, the reaction process was examined using in-situ DRIFTs. The study revealed the generation of -NH2 intermediates at the Lewis acid sites of the W: Ce 0.05 catalyst. These intermediates subsequently underwent reactions with gaseous NO via the Eley-Rideal mechanism. This approach not only amplified the low-temperature catalytic efficacy of the catalysts but also bolstered their resilience to SO2, thereby fostering the long-term stability of the NH3-SCR reaction.

Effect of metal elements doping on the CePO4 catalysts for selective catalytic reduction of NO with NH3

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Influence of different preparation methods on the activity of Ce and Mo co-doped ZSM-5 catalysts for the selective catalytic reduction of NOx by NH3

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Influence of CePO 4 with Different Crystalline Phase on Selective Catalytic Reduction of NO X with Ammonia

Comparative study of 3D ordered macroporous Ce0.75Zr0.2M0.05O2−δ (M = Fe, Cu, Mn, Co) for selective catalytic reduction of NO with NH3

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

The Promoting Effects of Amorphous CePO 4 Species on Phosphorus-Doped CeO 2 /tio 2 Catalysts for Selective Catalytic Reduction of NO X by NH 3

Molybdenum oxide as an efficient promoter to enhance the NH3-SCR performance of CeO2-SiO2 catalyst for NO removal

Mo-Doped Ce/GE Catalyst for Selective Catalytic Reduction of NOx by NH3

Comparative Study Of 3d Ordered Macroporous Ce0.75zr0.2m0.05o2-Delta (M = Fe, Cu, Mn, Co) For Selective Catalytic Reduction Of No With Nh3

Novel MoO3/CeO2–ZrO2 Catalyst for the Selective Catalytic Reduction of NOx by NH3

Promotional effects of phosphotungstic acid on CePO4 catalyst for the selective catalytic reduction of NO with NH3

Effects of doping Mn, Cu and Fe oxides on polyhedron CeO2 catalyst during NH3-SCR reaction

Sb-Containing Metal Oxide Catalysts for the Selective Catalytic Reduction of NOx with NH3

Doping effect of rare earth metal ions Sm3+, Nd3+ and Ce4+ on denitration performance of MnO catalyst in low temperature NH3-SCR reaction

Promotional Effects on NH3-SCR Performance of CeO2–SnO2 Catalysts Doped by TiO2: A Mechanism Study

Activity and Characterization of Ce–Mo–Ti Mixed Oxide Catalysts Prepared by a Homogeneous Precipitation Method for Selective Catalytic Reduction of NO with NH3

Mn and Fe oxides co-effect on nanopolyhedron CeO2 catalyst for NH3-SCR of NO

Bimetallic Cerium–copper Nanoparticles Embedded in Ordered Mesoporous Carbons As Effective Catalysts for the Selective Catalytic Reduction of NO with NH3