Abstract:Electric arc furnace dust (EAFD) is a hazardous solid waste generated as a byproduct in the steelmaking process, containing significant amounts of zinc and iron, making it a primary secondary source of zinc. The separation of zinc and iron in an environmentally-friendly and efficient manner poses a crucial technological challenge for the safe disposal and resource utilization of EAFD, facilitating the recovery of valuable zinc and the direct reuse of iron as raw materials for ironmaking. In this study, a novel method for restructuring zinc-bearing phases into sulfated compounds through low-temperature roasting by introducing FeS in EAFD were proposed. Simultaneously, the iron-containing phases undergo a transformation into Fe 2 O 3 . Subsequently, efficient separation of zinc and iron is achieved through a leaching process using dilute sulfuric acid. The conditions for the theoretical transformation of zinc-containing phases into ZnSO 4 and iron-containing phases into Fe 2 O 3 in EAFD were determined by thermodynamic calculations incorporating FeS. The temperature range for sulfation calcination was determined to be within 550–700 °C based on TG-DSC analysis and the evaluation of SO 2 release during the decomposition of FeS. The optimal conditions for the roasting process were determined as an E/F ratio of 1:3, a temperature of 650 °C, and a duration of 3 h. In addition, the optimal conditions for the leaching process were determined as the addition of 1 mL of 1 M H 2 SO 4 and a liquid–solid ratio of 25 mL/g. Under these conditions, the extractions of Zn and Fe reached 95.33 % and 0.17 %, respectively. The mechanism of phase reconstruction from zinc-containing phases to sulfate phases in EAFD was thoroughly analyzed, revealing that the Zn species in EAFD were transformed into Zn 3 O(SO 4 ) 2 through solid–solid and gas–solid reactions, while the majority of Fe species in EAFD and FeS were converted into Fe 2 O 3 . Effective separation of zinc and iron was achieved by dissolving Zn 3 O(SO 4 ) 2 in diluted sulfuric acid while retaining Fe 2 O 3 in the residue. This study provides a fresh perspective on the recovery of zinc from zinc-containing solid waste resources, offering significant potential for the sustainable management and utilization of EAFD.

Enhanced Leaching of Zinc Ferrite by the Formation of a Solid Solution With Magnetite in Hydrochloric Acid Solution

Selective dissolution and kinetics of leaching zinc from lime treated electric arc furnace dust by alkaline media

FeS-assisted restructuring of zinc-bearing phases into sulfated compounds for efficient zinc extraction from hazardous electric furnace dust

Efficient extraction and separation of zinc and iron from electric arc furnace dust by roasting with FeSO<sub>4</sub>?7H<sub>2</sub>O followed by water leaching

Facile and complete sulfuric acid leaching of zinc ferrite assisted by copper powder: Leaching mechanism and kinetics investigation

Reduction of Ferric Ion from Zinc Hydrometallurgy Acid-Leaching Solution Using Zinc Sulfide Concentrate

Zinc in Secondary Dust of Rotary Hearth Furnace Recovered by Water Leaching and Acid Leaching

Oxygen-assisted zinc recovery from electric arc furnace dust using magnesium chloride

Effective separation of Zn, Fe, and Mn from roasting-water leaching solution of blast-furnace dust using a precipitation-solvent extraction process

Optimisation of hybrid process to recover zinc from electric arc furnace dust using design of experiment approach

Mineral Phase Reconstruction and Separation Behavior of Zinc and Iron from Zinc-Containing Dust

Comparative Study of Steel Mill Dust Leaching with Phosphoric Acid and Sodium Hydroxide

Phase Transformation and Zinc Extraction from Zinc Ferrite by Calcium Roasting and Ammonia Leaching Process

Separation of Zinc from Zinc Ferrite by Magnetization Roasting and Ammonia Leaching

Magnetic Ni-Zn spinel ferrite nanopowder from toxic Zn-bearing electric arc furnace dust: A promising treatment process

Pyrometallurgical Technology for Extracting Iron and Zinc from Electric Arc Furnace Dust

Effect of in-situ oxidation on the phase composition and magnetic properties of Fe3O4: Implications for zinc hydrometallurgy

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Reclamation of acid pickling waste: A facile route for preparation of single-phase Fe 3 O 4 nanoparticle

Enhancing Zero-Valent Iron (ZVI) Pulverization During Mechanical Milling: FeSx As Milling Aids

Experimental and Mechanism Research on Vacuum Carbothermal Reduction of Zinc-Containing Electric Arc Furnace Dust