Failure Analysis of Torsion Shaft of Air Starter to External Gear Box of an Aero-engine: A Case of Complete Shear

Mrityunjoy Hazra,A. K. Singh

DOI: https://doi.org/10.1007/s11668-023-01669-w

2023-06-17

Journal of Failure Analysis and Prevention

Abstract:Torsion shaft was found broken as strip operation of the air starter was completed, while air starter over-speeding message came on multiple functional display (MFD) during startup of an aero-engine. Two failed shaft parts were received by the investigating team for failure analysis. The failure of both the components has occurred under the influence of maximum shear stress acting perpendicular to the shaft major axis. The fracture surfaces show the presence of shear dimples, the extent of which increases from center to periphery of the shaft. Rubbing is observed across the major part, most likely due to the running of the shaft for few cycles even after the failure of the shaft. Microstructure, hardness values and chemical compositions of both failed shaft parts indicate that the material of construction is close to 30KhGSHA. Two distinct appearances with whitish and bluish color along with slight difference in dimensions as well as in microstructures (discontinuous and continuous banding) indicate the probability that the received failed parts belong to two different shafts. However, the parts are said to be from one single failed shaft only, as by the user. Thus, the above-mentioned differences have been ascribed to the local variations in thermo-mechanical processing employed and subsequent heat treatment. An additional factor may have been frictional heating which has altered the microstructures in localized regions.