Failure Analysis of a Fighter Jet Engine Compressor Blade Due to Foreign Object Damage and High-Cycle Fatigue

R. A. Marín,J. A. Escobar,J. Loboguerrero

DOI: https://doi.org/10.1007/s11668-021-01195-7

2021-08-20

Journal of Failure Analysis and Prevention

Abstract:Failures affecting the compressor components of jet engines are critical during their operation because they compromise flight reliability. Blades are one of the most critical components. They are subjected to high dynamic loads resulting from high rotational speeds and aerodynamic forces. A better understanding of the failure mechanisms that affect these components could provide a safer strategy in the operation and maintenance of jet engines. A fighter jet engine compressor blade failure was analyzed in this work. Mechanical, macroscopic, and microscopic observations were performed to identify deterioration of properties. SEM and EDS analysis were performed to assess crack propagation and to identify possible surface treatments performed during the manufacturing of the blade. The material of the blades was found to be martensitic stainless steel (AISI 403) and the blades presented an aluminized coating. A crack was identified to have started on the high-pressure side of the blade. Examination of the fractured surface indicates that the failure mechanism was fatigue. The presence of a dent on an edge of the fractured surface suggests that the cause of failure might have been foreign object damage (FOD) due to high-speed impact of one or more particles on the blade surface. The axial location of the failed blade inside the engine was such that the probability of suffering high-speed impact of hard particles ingested by the engine was not negligible. An analytical model is presented to determine if the stresses expected at the FOD location were high enough to cause fatigue failure of the blade.