Abstract:Electrochemical cells are the key technologies for construction of carbon neutral society to produce hydrogen from water and produce useful chemicals from carbon dioxide utilizing renewable energy. Copper species are the unique catalysts for electrochemical carbon dioxide reduction reaction (CO 2 RR) with capable of producing C2+ products such as ethanol and ethylene. Selective production of target chemical is one of the most important requirements for the catalysts, and addition of different elements and surface modifications have been reported to be beneficial for the selective production. In the present study, copper oxides-based catalysts prepared with electroless plating techniques were examined for electrochemical CO 2 RR. To conduct CO 2 RR at relatively high current densities, the catalysts were examined in the form of gas diffusion electrode (GDE). The Cu 2 O based GDE was prepared by the combination of physical vapor deposition and electroless plating on hydrophobized carbon paper coated with mesoporous carbon layer. After the electroless plating treatment, the metal precursors were successfully converted to core-shell structured electrocatalyst with Cu 2 O shell and Cu core. By introducing different elements such as aluminum to the precursor, metallic Cu, the different element added catalysts were successfully prepared in the shape of GDE. Addition of different element significantly improved durability of the core-shell structured catalysts and, as a result, faradaic efficiency of ethylene of 24 hours after starting electrolysis was increase from 32% to 47% under applying cathodic current of 260 mAcm -2 . Further surface modifications with Nafion enhanced the durability and the faradaic efficiency of ethylene maintained >50% for over 48 hours and reached about 60% in maximum. In the presentation, we will discuss about the detailed structure of the electrocatalysts, results of full-cell test, and longer durability test over 100 hours.

Construction of 3D copper-chitosan-gas diffusion layer electrode for highly efficient CO2 electrolysis to C2+ alcohols

Additive-Assisted Electrodeposition of Cu on Gas Diffusion Electrodes Enables Selective CO2 Reduction to Multicarbon Products

Additive-Assisted Electrodeposition of Cu on Gas Diffusion Electrodes Enables Selective CO 2 Reduction to Multicarbon Products

Converting CO 2 to multi-carbon products at >1 A/cm 2 using gas diffusion electrode based on commercial materials via transfer process engineering

Hydrophobic 1-octadecanethiol functionalized copper catalyst promotes robust high-current CO2 gas-diffusion electrolysis

Converting CO2 to Multi-Carbon Products at >1 A/cm2 Using Gas Diffusion Electrode Based on Commercial Materials Via Transfer Process Engineering

Porous Bilayer Electrode‐Guided Gas Diffusion for Enhanced CO2 Electrochemical Reduction

Efficient Electrocatalytic CO2 Reduction to C2+ Alcohols at Defect-Site-Rich Cu Surface

Gas diffusion enhanced electrode with ultrathin superhydrophobic macropore structure for acidic CO 2 electroreduction

Near-Electrode Concentration Gradients of Bicarbonate and pH within Porous Gas Diffusion Electrode for Optimized Selective CO2 Electroreduction to C2+ Products

(Invited) Electrocatalytic Reduction of Carbon Dioxide over Aluminum-Added Coppor Oxide Gas Diffusion Electrode

Self-supported copper-based gas diffusion electrodes improve the local CO2 concentration for efficient electrochemical CO2 reduction

Impact of gas diffusion layer architecture on the performances of Cu-based electrodes for CO 2 electroreduction to ethylene in flow reactors

Enhanced Carbon Monoxide Electroreduction to >1 A cm-2 C2+ Products Using Copper Catalysts Dispersed on MgAl Layered Double Hydroxide Nanosheet House-of-Cards Scaffolds

Copper hollow fiber electrode for efficient CO2 electroreduction

Hierarchically Conductive Electrodes Unlock Stable and Scalable CO2 Electrolysis

Steering Electrochemical Carbon Dioxide Reduction to Alcohol Production on Cu Step Sites

Intrinsically Conductive and Cu-Functionalized Polymer-Composite Membranes as Gas Diffusion Electrodes for CO2 Electroreduction

Electron‐Deficient Cu Sites on Cu3Ag1 Catalyst Promoting CO2 Electroreduction to Alcohols

Designing Surface and Interface Structures of Copper-Based Catalysts for Enhanced Electrochemical Reduction of CO2 to Alcohols

Hierarchical Copper with Inherent Hydrophobicity Mitigates Electrode Flooding for High-Rate CO2 Electroreduction to Multicarbon Products.