Abstract:Electrochemical CO2 reduction (eCO(2)R) into useful chemicals and fuels is extensively studied, but it faces challenges such as high activation energy, carbonation, lower reaction rate, and unstable operation in alkaline conditions. In contrast, electrochemical CO reduction (eCOR) can efficiently produce C2+ products through a two-step conversion process without requiring high activation energy and involving complex reaction routes like CO2 electroreduction. Therefore, Converting CO2 to CO and then to C2+ products can be a strategic approach to enhance activity, selectivity, and economic viability. However, eCOR demonstrates lower reaction rates and sluggish kinetic with planar electrodes due to its lower solubility and poor mass transport to the electrode surface, therefore, industrially relevant current densities are still far to reach. Flow-through gas diffusion electrodes (FTGDEs) can potentially solve the issue of poor mass transport due to their abundant surface area, porous structure, and improved triple-phase interface. Herein, electrochemical CO reduction to C2+ products is investigated using Cu-based FTGDEs. A comparison of eCOR with eCO(2)R is also carried out to study the catalytic activity, selectivity, and stability. To demonstrate the influence of particle size, FTGDEs are designed using varying Cu particle sizes i.e. 10 nm, 100 nm, and 10 mu m. The eCOR produced C2+ products with ethylene being the main product achieving 474 mA/cm(2) current density and 72% faradaic efficiency at -0.9 V vs. RHE, while eCO(2)R yielded more C-1 products with lower catalytic activity and selectivity. Compared to gas diffusion configuration, the poor catalytic activity and selectivity of eCOR are observed in non-gas diffusion configuration which signifies that, due to higher local CO concentration and improved triple-phase generation, higher performance of FTGDEs can be obtained from gas diffusion configuration. Finally, the stable operation of Cu electrodes during eCOR highlights its promise as a highly suitable candidate for enhancing eCOR towards higher carbon products.

Additive-Assisted Electrodeposition of Cu on Gas Diffusion Electrodes Enables Selective CO2 Reduction to Multicarbon Products

Additive-Assisted Electrodeposition of Cu on Gas Diffusion Electrodes Enables Selective CO 2 Reduction to Multicarbon Products

Atomic Layer Deposition of Cu Electrocatalysts on Gas Diffusion Electrodes for CO 2 Reduction

Self-supported copper-based gas diffusion electrodes improve the local CO2 concentration for efficient electrochemical CO2 reduction

Ampere-level CO2 reduction to multicarbon products over a copper gas penetration electrode

Facilitating electrocatalytic CO2 reduction through electrolyte additives accompanied by activation of copper electrode with cyclic voltammetry

Converting CO 2 to multi-carbon products at >1 A/cm 2 using gas diffusion electrode based on commercial materials via transfer process engineering

(Invited) Electrocatalytic Reduction of Carbon Dioxide over Aluminum-Added Coppor Oxide Gas Diffusion Electrode

Converting CO2 to Multi-Carbon Products at >1 A/cm2 Using Gas Diffusion Electrode Based on Commercial Materials Via Transfer Process Engineering

CuC(O) Interfaces Deliver Remarkable Selectivity and Stability for CO2 Reduction to C2+ Products at Industrial Current Density of 500 mA cm−2

Polyacrylate modified Cu electrode for selective electrochemical CO2 reduction towards multicarbon products

Analyzing the Electrochemical Reduction of CO and CO2 As Reactants to C1 and C2 Products on Copper-Based Flow-Through Gas Diffusion Electrodes

Direct Low Concentration CO2 Electroreduction to Multicarbon Products Via Rate-Determining Step Tuning

Changing the Product Selectivity for Electrocatalysis of CO2 Reduction Reaction on Plated Cu Electrodes

Enhanced electroreduction of CO2 to C2+ products on heterostructured Cu/oxide electrodes

Unveiling the Synergistic Effect between Graphitic Carbon Nitride and Cu 2 O toward CO 2 Electroreduction to C 2 H 4

Impact of gas diffusion layer architecture on the performances of Cu-based electrodes for CO 2 electroreduction to ethylene in flow reactors

Multi‐Shell Copper Catalysts for Selective Electroreduction of CO2 to Multicarbon Chemicals

Hydrophobic 1-octadecanethiol functionalized copper catalyst promotes robust high-current CO2 gas-diffusion electrolysis

Boosting Electrochemical CO2 Reduction Via Surface Hydroxylation over Cu-Based Electrocatalysts

Construction of 3D copper-chitosan-gas diffusion layer electrode for highly efficient CO2 electrolysis to C2+ alcohols