High-strength and thermally stable TiB2-modified Al–Mn–Mg–Er–Zr alloy fabricated via selective laser melting
Jiang Yu,Yaoxiang Geng,Yongkang Chen,Xiao Wang,Zhijie Zhang,Hao Tang,Junhua Xu,Hongbo Ju,Dongpeng Wang
DOI: https://doi.org/10.1007/s12613-024-2879-7
2024-09-02
International Journal of Minerals Metallurgy and Materials
Abstract:To increase the processability and plasticity of the selective laser melting (SLM) fabricated Al–Mn–Mg–Er–Zr alloys, a novel TiB 2 -modified Al–Mn–Mg–Er–Zr alloy with a mixture of Al–Mn–Mg–Er–Zr and nano-TiB 2 powders was fabricated by SLM. The processability, microstructure, and mechanical properties of the alloy were systematically investigated by density measurement, microstructure characterization, and mechanical properties testing. The alloys fabricated at 250 W displayed higher relative densities due to a uniformly smooth top surface and appropriate laser energy input. The maximum relative density value of the alloy reached (99.7 ± 0.1)%, demonstrating good processability. The alloy exhibited a duplex grain microstructure consisting of columnar regions primarily and equiaxed regions with TiB 2 , Al 6 Mn, and Al 3 Er phases distributed along the grain boundaries. After directly aging treatment at a high temperature of 400°C, the strength of the SLM-fabricated TiB 2 /Al–Mn–Mg–Er–Zr alloy increased due to the precipitation of the secondary Al 6 Mn phases. The maximum yield strength and ultimate tensile strength of the aging alloy were measured to be (374 ± 1) and (512 ± 13) MPa, respectively. The SLM-fabricated TiB 2 /Al–Mn–Mg–Er–Zr alloy demonstrates exceptional strength and thermal stability due to the synergistic effects of the inhibition of grain growth, the incorporation of TiB 2 nanoparticles, and the precipitation of secondary Al 6 Mn nanoparticles.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing