The Microstructure and Mechanical Behaviors of the Ti–6.5Al–3.5Mo–1.5Zr–0.3Si Alloy Produced by Laser Melting Deposition

Zheng Liu,Zuo-Xiang Qin,Fang Liu,Xing Lu,Hua-Ming Wang

DOI: https://doi.org/10.1016/j.matchar.2014.09.002

IF: 4.537

2014-01-01

Materials Characterization

Abstract:The microstructure and mechanical properties of the Ti–6.5Al–3.5Mo–1.5Zr–0.3Si alloy produced by laser melting deposition have been investigated. The columnar grains of the Ti–6.5Al–3.5Mo–1.5Zr–0.3Si alloy due to the layer-by-layer epitaxial growth from the underlying template grains during laser melting deposition, which is roughly parallel to the deposition direction, had been found by optical microscopy; strong 101¯2α crystallographic texture has been confirmed by X-ray diffraction and electron backscattered diffraction. Depending on the last heating history, the microstructure of the alloy undergoes a continued change opposite to the deposition direction: martensitic α′ (transformed β); coarsened primary α laths with transformed β; coarsened primary α laths; and the fine basketweave microstructure with a few coarsened α laths or annealed martensitic α′. The average Vickers micro-hardness value of the alloy is 364HV. The alloy parallel to the deposition direction presents lower tensile strength (925MPa) and better elongation (18.8%), compared with 1025MPa and 8.2% of that vertical to the deposition direction, which has been discussed using its microstructure characterization.