Influence of titanium ion doping on structural changes in porous hydroxyapatite ceramics

Takashi Iwamoto,Yasumichi Kogai

DOI: https://doi.org/10.1016/j.solidstatesciences.2023.107222

IF: 3.752

2023-06-03

Solid State Sciences

Abstract:Biocompatible titanium (Ti) is commonly used as an implant material. Hydroxyapatite (HAp, Ca 10 (PO 4 ) 6 (OH) 2 ) is a biomaterial that is similarly applied in the medical field owing to its biocompatibility. HAp is used as an alternative material for bones and teeth; for such purpose, the pores should have diameters of at least 200 μm. However, no studies have reported porous Ti-doped HAp. In this study, we fabricated five types of porous Ti-doped HAp ceramics using different amounts of 30% titanium sulfate solution (0.1, 0.2, 0.3, 0.4, and 0.5 g) as additive Ti ions in the chemical route. In general, the lattice parameters of Ti-doped HAp decrease because Ti ions are substituted for Ca ions but have a smaller ionic radius. However, the lattice parameters a and c actually increased in the porous Ti-doped HAp ceramics produced in this study, and only decreased in sample fabricated with 0.5 g of Ti solution. This change in structure was attributed to dehydroxylation of OH ions from the HAp lattice. Ti ions inserted into OH channels parallel to the c -axis in HAp lattices generate O–Ti–O bonds. Consequently, the lattice parameter c increased. The interaction between the dislocated OH ions and protonated HPO 4 ions in the HAp lattices increased the lattice parameter a . The formation of O–Ti–O bonds did not maintain the charge balance, owing to the tetravalent Ti ions. However, the development of the c -plane in the HAp lattices increased as the amount of added Ti increased. Consequently, the growth of the negatively charged c -plane maintained the charge balance by compensating for the extra charges of the Ti ions.

chemistry, physical, inorganic & nuclear,physics, condensed matter