Abstract:Direct ink writing (DIW) of aerogels has great potential in designing novel three-dimensional (3D) multifunctional materials with hierarchical structures ranging from the nanoscale to the macroscopic scale. In this paper, pure aerogels composed of inorganics, strongly cross-linking organics, and weakly cross-linking organics were directly written via the precise control of the gelation degree without using any additives. The rheological properties of a resorcinol–formaldehyde aerogel-based sol–gel ink (marked as RA ink) were measured at different reaction times to determine the suitable printable range (G′LVR: several 103 Pa) that ensures its good print fidelity. In addition, the rheological evolution of the RA ink during the sol–gel process and under different shear stresses was studied. The correlation of relevant parameters was established according to the Hagen–Poiseuille model. Other typical aerogel-based sol–gel inks including a silica aerogel-based sol–gel ink (SA ink) and a polyimide aerogel-based sol–gel ink (PA ink) for DIW were also demonstrated. Finally, water evaporation experiments were carried out using a 3D-printed carbonized resorcinol–formaldehyde aerogel (CA) to further exhibit the potential applications of this novel technology in solar steam generation. The evaporation rate (1.57 kg m–2 h–1) and efficiency (88.38%) of 3D-printed CA were higher than those of bulk CA (1.21 kg m–2 h–1 and 69.82%). This paper systematically studies the control of DIW parameters for aerogel-based sol–gel inks and shows a potential application in high-efficiency 3D-printed evaporators.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c03312?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c03312</a>.Rheological behaviors and thixotropic behaviors of RA inks (Figure S1); rheological behaviors of the SA ink and the PA ink (Figure S2); rapid solidification of the PA ink once it met water (Figure S3); Herschel–Buckley model for RA inks (Figure S4); study of relevant parameters in DIW (Figure S5); extrusion experiments for dextrin (Figure S6); extrusion experiments for RA inks (Figure S7); 3D-printed hydrogels using the RA ink, SA ink, and PA ink (Figure S8); TG-DSC tests for 3D-printed aerogels (Figure S9); uniaxial compression–decompression test for 3D-printed aerogels (Figure S10); derivation of the correlation of the relevant parameters; filament widths at varied applied pressures and writing speeds (Table S1); filament widths at varied heights of the needle to the substrate (Table S2); pressure value, maximum shear stresses, and yield stresses for dextrin and RA inks (Table S3); detailed parameters of bulk CA and 3D-printed CAs (Table S4); and water evaporation data of 3D-printed CAs, bulk CA, and pure water (Table S5).This article has not yet been cited by other publications.

Direct Ink Writing of Tubular Al2O3 Membrane Support Using Agar-Based Ink in 3D-Printing

A Systematic Thermal Analysis for Accurately Predicting the Extrusion Printability of Alginate-Gelatin-Based Hydrogel Bioinks

Dissipative Particle Dynamics of Nano-Alumina Agglomeration in UV-Curable Inks

Optimization of 3D Printing Parameters for Alumina Ceramic Based on the Orthogonal Test

Fabrication of alumina ceramic membrane supports using LCD 3D printing and titania nanoparticle doping

A novel experimental approach to quantitatively evaluate the printability of inks in 3D printing using two criteria

3D gel printing of alumina ceramics followed by efficient multi-step liquid desiccant drying

3D Printing of Bioinspired Alginate‐Albumin Based Instant Gel Ink with Electroconductivity and Its Expansion to Direct Four‐Axis Printing of Hollow Porous Tubular Constructs without Supporting Materials

Preparation, Mechanical and Biological Properties of Inkjet Printed Alginate/Gelatin Hydrogel

A thermogelling organic-inorganic hybrid hydrogel with excellent printability, shape fidelity and cytocompatibility for 3D bioprinting

Direct ink writing of aloe vera/cellulose nanofibrils bio-hydrogels

Characterization of Alginate-Gelatin-Cholesteryl Ester Liquid Crystals Bioinks for Extrusion Bioprinting of Tissue Engineering Scaffolds

Reinforced 3D Composite Structures of γ-, α-Al2O3 with Carbon Nanotubes and Reduced GO Ribbons Printed from Boehmite Gels

Investigating the effect of polymer additives on the rheology of SiC/clay paste for use in Direct Ink Writing method

Engineering alginate as bioink for bioprinting

Three-Dimensional-Printed Silica Aerogels for Thermal Insulation by Directly Writing Temperature-Induced Solidifiable Inks

Optimization of the sintering thermal treatment and the ceramic ink used in direct ink writing of α-Al2O3: Characterization and catalytic application

Versatile Direct Writing of Aerogel-Based Sol–Gel Inks

Improving printability of hydrogel-based bio-inks for thermal inkjet bioprinting applications via saponification and heat treatment processes

Direct-ink-writable nanocellulose ternary hydrogels via one-pot gelation with alginate and calcium montmorillonite

Sodium Alginate/Gelatine Hydrogels for Direct Bioprinting—The Effect of Composition Selection and Applied Solvents on the Bioink Properties