Abstract:A successful 3D printable hydrogel ink needs not only biofunctionalities but also minimal fabrication steps such as multiple crosslinking sites, high printability, cytocompatibility, high shape fidelity, stability, shear thinning, robust properties, and less time-consuming processing steps, by maximizing known material chemistries and functionalities. This work reports a novel bioinspired conjugate with polysaccharide (alginate)–tannic acid (TA)–protein (bovine serum albumin) to fabricate proteoglycan-like gels, which are 3D printable with multilayers, shear-thinning, elastic, electroconductive (with carbon nanotubes), controlled crosslinking/degradation through multiple crosslinking mechanisms (TA, Ca2+ ions, and NaIO4 oxidation), and interactions with cytocompatible hydrogel system. The synthesis process is simple, and gelation (within 2 h) is ensured without any chemical crosslinking agents (at room temperature). While cell-adhesive albumin largely improves cytocompatibility, carbon nanotubes in the gel give electrical conductivity in the different four-axis 3D printed structures, including large hollow tubular constructs. This work demonstrates promising results of electroconductive proteoglycan-like gel ink to address the challenges in 3D/four-axis ink printing such as synthesis, printability, shape fidelity, electroconductivity, controlled fabrication and degradation, cytocompatibility, and multiple crosslinking abilities to maintain the dimensions of the diversely printed constructs.

What problem does this paper attempt to address?

The main problems that this paper attempts to solve are some key challenges existing in current 3D - printed hydrogel inks in biomedical applications. Specifically, these challenges include: 1. **Complicated synthesis steps**: Traditional 3D - printed hydrogel inks require multiple chemical derivatization steps, such as chemical modification of polymers, multi - step preparation processes, initiators, toxic chemical cross - linkers, etc. These steps are not only time - consuming but also difficult to optimize. 2. **Insufficient shape fidelity and mechanical properties**: Although low - viscosity hydrogels are easy to print, their structures often have lower mechanical properties and shape fidelity, and cannot achieve multi - layer printing and self - supporting structures. 3. **Lack of electrical conductivity and cell compatibility**: Existing 3D - printed hydrogel inks usually do not have electrical conductivity, and are also deficient in cell compatibility and multi - cross - linking ability. 4. **Limitations of four - axis 3D printing**: Especially for the four - axis 3D printing technology using natural polymers, it is difficult to print large - scale hollow tubular structures without using support materials. To solve these problems, the author has developed a new bio - inspired sodium alginate - tannic acid - bovine serum albumin (Alginate - Tannic Acid - Albumin, AlTaB - ABT) conjugated material for manufacturing 3D - printed inks. This ink has the following characteristics: - **Multi - layer printing and shear - thinning**: It can achieve multi - layer 3D printing and has shear - thinning properties, which is convenient for extrusion printing. - **Elasticity and electrical conductivity**: By adding carbon nanotubes (CNT), the ink is endowed with electrical conductivity. - **Controllable cross - linking and degradation**: Controllable cross - linking and degradation are achieved through multiple cross - linking mechanisms (tannic acid, Ca²⁺ ions and NaIO₄ oxidation). - **Cell compatibility**: The addition of bovine serum albumin (BSA) improves cell compatibility. - **Self - supporting structures without support materials**: It can print complex self - supporting structures, including large - scale hollow tubular structures, without using support materials. Through these improvements, this research aims to develop an efficient and multi - functional 3D - printed hydrogel ink to meet various needs in the biomedical and tissue engineering fields.

3D Printing of Bioinspired Alginate‐Albumin Based Instant Gel Ink with Electroconductivity and Its Expansion to Direct Four‐Axis Printing of Hollow Porous Tubular Constructs without Supporting Materials