Multi-scale Progressive Damage and Failure Behavior Analysis of Three-Dimensional Winding SiC Fiber-Reinforced SiC Matrix Composite Tube
Jianhui Pu,Jun Wang,Jianbo Tang,Liangliang Shen,Qing Huang,Ning Hu,Qiang Wei,Jian Xu
DOI: https://doi.org/10.1007/s10443-023-10129-5
IF: 2.3
2023-06-17
Applied Composite Materials
Abstract:Continuous silicon carbide fiber-reinforced silicon carbide matrix (SiC f /SiC) composites are widely used in nuclear fuel cladding due to their excellent physical and chemical properties. The application of nuclear energy puts forward higher requirements on the structural stability and mechanical properties of SiC f /SiC components. Therefore, in this study, a multiscale analysis strategy considering the microscopic interface parameters and mesoscopic structure response to the failure of ceramic matrix composites (CMCs) was constructed for in-depth investigation of the failure behavior mechanism of CMCs. Among them, a microscopic representative volume element model coupled with a phase field fracture approach and a cohesion zone model was used to capture matrix brittle cracking and fiber/matrix debonding behaviors. The progressive damage behavior of fiber/matrix interfacial strength on unidirectional CMCs (UD-CMCs) was investigated. The results show that the presence of a weak interface causes a dramatic decrease in the strength of UD-CMCs by 70%. Based on the real winding path of three-dimensional (3D) filament, a 3D wound SiC f /SiC tube model reflecting the overlapping effect between fiber bundles was established, and by combining with the matrix cracking theory and LaRC05 failure criterion, the effect of winding angle on the mechanical properties of 3D wound SiC f /SiC tube was studied. The results reveal that the established 3D winding model can capture not only the overall response, but also the local response, providing an effective tool for the structural design, failure analysis, and safety service design of CMC components.
materials science, composites