Abstract:The objective of the present work is to analyze "in situ" the phase transformations associated to martensite-to-austenite and vice versa during post-weld heat treatments (PWHTs) of the weld metal of supermartensitic welding consumable, considering two different initial microstructures. For this purpose, a coupon was welded with 1,7 kJ/mm of heat input, using the semiautomatic arc welding process with Ar + 5% He as shielding gas. The filler metal was a 1.2-mm diameter metal-cored tubular wire, which contains 12.5%Cr, 6.7%Ni, and 2.5%Mo (% by weight). Two initial microstructural conditions were analyzed: as welded (AWC) and as solubilized at 1000 °C, 60 minutes (ASC). Under these conditions, two different PWHTs involving simple (intercritical: 665 °C, 15 minutes) and double tempering (intercritical: 665 °C, 15 minutes + subcritical: 590 °C, 15 minutes) were carried out. To study the microstructural evolution during PWHT, "in situ" x-ray diffraction was performed using synchrotron radiation, measuring every 3.15 seconds during heating, holding, and cooling. For intercritical tempering, the solubilization increased the start austenite temperature during heating from 618.7 to 665 °C, and increased the start martensite temperature during the cooling from 128 to 248 °C. The reformed austenite at room temperature was higher for the AWC condition than for the ASC condition for both intercritical tempering (25.7 and 9.6%, respectively) and second subcritical tempering (46 and 26%, respectively). Nevertheless, a higher amount of both reverted and reformed austenite was formed during the heating at 590 °C for the ASC. This is correlated to the lower macrostrain of the reformed austenite for ASC, suggesting that formation modes of reverted austenite are different. Furthermore, although for both conditions, the kinetic exponent n of the Johnson–Mehl–Avrami–Kolmogorov (JMAK) model indicates diffusion-controlled unidimensional growth with decreasing nucleation rate, both the n parameter and equilibrium volume fraction of transformed austenite are higher for the ASC condition than for the AWC condition.

Detection of Phase Transformation during Plastic Deformation of Metastable Austenitic Steel AISI 304L by Means of X-ray Diffraction Pattern Analysis

Coupled microscopic and micromagnetic depth-specific analysis of plastic deformation and phase transformation of metastable austenitic steel AISI 304L by flow forming

Phase transformations in cold-rolled 304L stainless steel by dilatometry

In-situ Investigation Via High Energy X-ray Diffraction of Stress-Induced(0002)α→(110)β Transformation in a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr Alloy

Optical Detection of Phase Transformations in Steels: An Innovative Method for Time-Efficient Material Characterization During Tailored Thermo-mechanical Processing of a Press Hardening Steel

Identification and quantification of martensite in ferritic-austenitic stainless steels and welds

Grain-orientation-dependent Phase Transformation Kinetics in Austenitic Stainless Steel under Low-Temperature Uniaxial Loading

Tracing Phase Transformation And Lattice Evolution In A Trip Sheet Steel Under High-Temperature Annealing By Real-Time In Situ Neutron Diffraction

The In Situ Observation of Phase Transformations During Intercritical Annealing of a Medium Manganese Advanced High Strength Steel by High Energy X-Ray Diffraction

Effect of Phase Transformation on Damage-Induced Magnetization of 304 Austenitic Stainless Steel

Evidence of dynamic ferrite transformation during thermomechanical simulation of an X70 microalloyed steel above Ae 3 temperature

The Investigation of Strain-Induced Martensite Reverse Transformation in AISI 304 Austenitic Stainless Steel

Grain-level effects on in-situ deformation-induced phase transformations in a complex-phase steel using 3DXRD and EBSD

Influence of phase transformations on the mechanical properties of austenitic stainless steels

In Situ Synchrotron X-ray Diffraction Analysis During Post-Weld Heat Treatments of Supermartensitic Stainless Steel Weld Metal

Neutron Diffraction and Crystal Plasticity Analysis on Q&P Steel in Deformation

In-situ Observation of Phase Transformation During Heat Treatment Process of High-Carbon Bainitic Bearing Steel

X-ray diffraction for phase identification in Ti-based alloys: Benefits and limitations

In situ 3D crystallographic characterization of deformation-induced martensitic transformation in a metastable Fe–Cr–Ni austenitic alloy by X-ray microtomography

In situ neutron diffraction and crystal plasticity analysis on Q&P1180 steel during plastic deformation

Influence of the martensitic transformation on the deformation behaviour of an AISI 316 stainless steel at low temperatures