Investigations on Silicon Carbide Reinforced High Entropy Alloy (CoCrNiMnFe) matrix Composites Produced by Powder Metallurgy Process
D. Pritima,G. Veerapppan,M. Ravichandran,S. Rajamuneeswaran
DOI: https://doi.org/10.1007/s12633-023-02369-8
IF: 3.4
2023-03-11
Silicon
Abstract:Powder Metallurgy route was employed to produce high entropy alloys Co–Cr–Ni-Mn–Fe–SiC x where x indicates the weight percentage of SiC. This investigation shows the different proportion of SiC content ( x = 2 wt.%, 4 wt.% and 6 wt.%) added in Co–Cr–Ni-Mn–Fe– powders. The trial samples were compacted using a press and subjected to sintering at two distinct temperatures ( T sint ) 1250° and 1350 °C respectively.T he composites were subjected to characterization technique such as optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and atomic force microscopy. These HEA alloys were analyzed for the distribution of SiC in HEA matrix using SEM and it was observed that the distribution of SiC was homogeneous, as shown in the matrix. The synthesized SiC reinforced composites are subjected to compression test, hardness test and corrosion test. The densification behavior was examined on the sintered specimens. The post sintering process study indicates that the density of HEA- 0 wt.% SiC, HEA-2 wt.% SiC, HEA- 4 wt.% SiC, and HEA-6 wt.% SiC composites, which was sintered at 1350 °C, are 7.38, 7.05, 6.73 and 6.41, respectively. Co–Cr–Ni-Mn–Fe HEA alloys sintered at 1350 °C have density of 0.66% greater than alloys sintered at 1250 °C.Co–Cr–Ni-Mn–Fe-4 wt.% SiC alloy sintered at 1350 °C and the properties like compression strength, corrosion resistance and hardness are found to be very high. Unreinforced Co–Cr–Ni-Mn–Fe alloy sintered at 1350 °C exhibits sinterability of 0.89.Among the composites sintered at 1250 °C and 1350 °C, Co–Cr–Ni-Mn–Fe-2 wt.% SiC exhibit highest sinterability of 0.81. The ball milled powder morphology was analyzed using SEM and elemental presence of Cr, Co, Mn, Ni, Fe, and SiCin the matrix was confirmed and verified by the energy dispersive spectroscopy (EDS) analysis. The HEA composite (Co–Cr–Ni-Mn–Fe- 4 wt.% SiC composite) sintered at 1350 °C exhibits the best corrosion resistance which was determined by the potentiodynamic investigation.
materials science, multidisciplinary,chemistry, physical