Abstract:Purpose. Justification of mechanism of the structure transformations in the carbon steel of the railway wheel during disk thermal strengthening. Research methods. The material for the study was carbon steel of a railway wheel with a content of 0.57 % C, 0.65 % Si, 0.45 % Mn, 0.0029 % S, 0.014 % P and 0.11 % Cr. The railway wheel was heated to temperatures higher than Ac3, kept at this temperature to complete austenite homogenization process, and disk was rapidly cooled to the specified temperature. Degree defectiveness structure of the metal after accelerated cooling was assessed using technique of X-ray structural analysis. Strength stress, yield stress and relative elongation of the carbon steel were determined at stretching at rate of deformation 10-3 s-1. Results. At accelerated cooling of the carbon steel, the sources of strengthening are the processes of blocking mobile dislocations due to the condensation of carbon atoms on them and dispersion strengthening from the formed particles of the carbide phase. At temperatures of termination of forced cooling of carbon steel above 300...350 °C, the reduction rate of strength properties is determined by the excess of total effect of softening from decomposition of the solid solution, acceleration of spheroidization and coalescence of cementite particles over the blocking of dislocations by carbon atoms and dispersion hardening. Scientific novelty. The level of strength and plasticity characteristics of carbon steel of the railway wheel disc, depending on the temperature end forced cooling, is determined by the ratio of the influence of degree super saturation of the solid solution and the dispersion strengthening by carbide phase. Practical value. For temperatures termination of accelerated cooling of 200...300 °C, degree of super saturation of the solid solution is the main factor that determines the level of strength and plasticity characteristics. When manufacturing an all-rolled railway wheel, the strength limit of the disc metal can be increased by accelerated cooling to the middle range of temperature.

White Layer in M76 High Carbon Rail Steel: Formation Mechanism and Properties

Hybrid structure of white layer in high carbon steel – Formation mechanism and its properties

Heterogenous structure and formation mechanism of white and brown etching layers in bainitic rail steel

Phase and Microstructural Evolution in White Etching Layer of a Pearlitic Steel During Rolling–sliding Friction

Formation Mechanism of Brown Etching Layers in Pearlitic Rail Steel

A Novel Mechanism of the Formation of White and Brown Etching Layer in Bainitic Rail Steel

Influence of thermal loading parameters and microstructure on the formation of stratified surface layers on railway wheels

Microstructure of the Worn Surfaces of a Bainitic Steel Railway Crossing

Microstructure characteristics and formation mechanisms of white etching layer (WEL) and brown etching layer (BEL) on martensite bearing raceway

Influence of stratified tribologically transformed structure layers on contact fatigue crack initiation of bainitic rail steel

The nature of the white-etching surface layers produced during reaming ultra-high strength steel

Evaluation of Mechanisms for Strengthening of Surface Layers of Long Rails in Different Directions Under Continuous Operation

Stratified surface layers affecting crack propagation in wheel-rail contacts

INFLUENCE HOT PLASTIC DEFORMATION ON THE STRUCTURE AND PROPERTIES OF CARBON STEEL OF THE RAILWAY WHEEL

Damage evolution around white etching layer during uniaxial loading

Rolling Contact Fatigue Damage in Welded Rail Steel Joints

Wear behavior of carbon steels under high-stress impact

Analysis of hardening mechanisms of rail steel under plastic deformation by uniaxial compression

Characterization of the Microstructure Changes Induced by a Rolling Contact Bench Reproducing Wheel/Rail Contact on a Pearlitic Steel

STRUCTURAL CHANGES DURING THERMAL STRENGTHENING OF THE RAILWAY WHEEL

Consequences of thermite welding on the microstructure of the heat affected zone of a carbide-free bainitic steel rail