Abstract:MxV Rail has explored new methods of improving the longevity of both rail and thermite welds. As a part of this research, MxV Rail explored ultrasonic impact treatment (UIT) as a method for increasing thermite weld performance and performed a residual stress investigation to estimate the distribution of the compressive and tensile stresses along the weld cross sections. UIT uses a needle to impart very small and rapid localized impacts to plastically deform the material it is applied to. Weld material reshaping and compressive residual stresses all result from UIT, which produce fatigue life improvements that benefit the life of the weld. A residual stress investigation using latest methods was also executed on both new rails and rails with different amounts of wear to analyze the distribution of estimated stresses. Fatigue defects grow quickly under tensile stresses and slowly under compressive stresses. Since UIT introduces compressive stresses on the surfaces of the weld material, an increase in the life of thermite welds can be expected due to retarded crack growth in localized areas of compressive stresses. In order to estimate the change in stress conditions caused by UIT, MxV Rail analyzed residual stresses in three thermite welds: (1) a UIT-treated new weld, (2) a UIT-treated weld removed from track after 150 million gross tons, and (3) an untreated new thermite weld. The residual stress estimations were accomplished by using hole drilling (HD) and contour methods. While the HD method provides estimated strains along two axes (longitudinal and transverse) at very shallow depths in particular locations, the contour method involves wire electric discharge machining and advanced finite element analysis to estimate the overall longitudinal strains ( ε zz ) across the entire cross section of the weld or rail. The contour method was also applied to the rails to better understand the influence of residual stresses due to wheel–rail interaction on the head along with rail wear and how the modified residual stress distribution in worn rail compares to the initial residual stress distribution in a new rail that has been rolled but not laid in track.

Consequences of thermite welding on the microstructure of the heat affected zone of a carbide-free bainitic steel rail

Effect of microstructure on wear and rolling contact fatigue behaviors of bainitic/martensitic rail steels

The effect of microstructure evolution on the ratchetting-fatigue interaction of carbide-free bainite rail steels under different heat-treatment conditions

Study on microstructure and mechanical properties of continuous drive friction-welded joints of bainitic rail steel

Decomposition mechanisms of continuously cooled bainitic rail in the critical heat-affected zone of a flash-butt welded joints

Effect of Non-Uniform Microstructure on Rolling Contact Fatigue Performance of Bainitic Rail Steel

Microstructure of the Worn Surfaces of a Bainitic Steel Railway Crossing

Experimental Investigation on Microstructures and Mechanical Properties of PG4 Flash-Butt Rail Welds

Influence of stratified tribologically transformed structure layers on contact fatigue crack initiation of bainitic rail steel

Effect of intrinsic thermal cycles on the microstructure and mechanical properties of heat affect zones in laser cladding coatings on full-scale rails

Reduced spheroidization in rail flash-butt welding by selective alloying

INFLUENCE HOT PLASTIC DEFORMATION ON THE STRUCTURE AND PROPERTIES OF CARBON STEEL OF THE RAILWAY WHEEL

High cycle fatigue properties and fatigue crack propagation behavior of a bainite railway axle steel

Influence of CDFW Process Parameters on Microstructure and Mechanical Properties of U75V Rail Steel Welded Joint

Experimental and simulation study of phase transformation in thermite welded railway steel heat-affected zone regions

Residual Stress Estimation Using Hole Drilling and Contour Methods in Rail Welds Treated with and without Ultrasonic Impact Treatment

Characterization of the Microstructure Changes Induced by a Rolling Contact Bench Reproducing Wheel/Rail Contact on a Pearlitic Steel

Relationship between Microstructure and Properties of 1380 MPa Grade Bainitic Rail Steel Treated by Online Bainite-Based Quenching and Partitioning Concept

High-silicon spring steel transformation to carbide-free bainitic (CFB) steel: a mechanical and tribological approach under rolling/sliding conditions

PROCESSES OF WELDED JOINT STRUCTURE FORMATION DURING ELECTRIC RESISTANCE WELDING OF RAILWAY RAILS

Sliding Wear and Low Cycle Fatigue Properties of New Carbide Free Bainitic Rail Steel