Abstract:The non-contact electrical resistivity method was employed to investigate the microstructural development of three grades of cement under a fixed water-to-cement ratio (w/c) and the same curing conditions. The method was verified by measuring the heat of hydration and estimating the degree of hydration of the three pastes. The results showed that the existence of a linear relationship between the compressive strength at 28 d (f 28) and bulk electrical resistivity at 72 h (ρ72); thus, the proposed method can be used to assess the strength of cement. Moreover, the results indicated that the quality of cement can be further distinguished by interpreting the trend in the resistivity curve. The high-strength cement will have lower electrical resistivity values during cement dissolution due to the higher content of ions in the pore solution, while it will have higher resistivity values during cement hardening due to the greater amount of hydrates. The electrical resistivity of the cement solution (ρ0) filtered from the cement paste at an early age was measured to demonstrate the effect of the ionic concentration on the bulk electrical resistivity in the initial hydration period. The measured liquid resistivity of cement can be used as an indication of clinker reactivity; higher-strength cement will always have lower measured values. The rate of electrical resistivity development curve was plotted to elucidate the setting range of cement pastes based on three critical points. The time at the second critical point (C2) coincided with the final setting time determined using a Vicat needle. New general relationships between the gel-space ratio and electrical resistivity were developed. Furthermore, autogenous shrinkage was measured for the three cement pastes, and the behaviour could be anticipated from the electrical resistivity measurements.

Monitoring the hydration behavior of hardened cement paste affected by different environmental pH regimes

A Mathematical Model for the Electrical Resistivity of Cement Paste at Early Ages Considering the Partially Saturated State

Monitoring the Setting and Hardening Behaviour of Cement Paste by Electrical Resistivity Measurement

Early Hydration Process of Portland Cement Paste by Electrical Measurement

Monitoring of Hydration Using the Electrical Resistance of Carbon Fiber Reinforced Cement Materials

Portland Cement Hydration by Electrical Resistivity Method and Computer Simulation

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

Resistivity Method for Monitoring the Early Age Pore Structure Evolution of Cement Paste

Electrochemical Impedance Spectroscopy Monitoring of Hydration Behaviors of Cement with Na2CO3 Accelerator

Investigation of the Early-Age Microstructural Development of Hydrating Cement Pastes Through Electrical Resistivity Measurements

Simple Three-Step Analytical Scheme for Prediction of Elastic Moduli of Hardened Cement Paste

Non-Destructive Monitoring of Hydration Characteristics in Alternative Materials and Seawater-Based Cementitious Pastes Using Electrochemical Impedance Spectroscopy

Influence of Calcium Sulfate State and Fineness of Cement on Hydration of Portland Cements Using Electrical Measurement

STUDY ON HYDRATION OF PORTLAND CEMENT USING AN ELECTRICAL RESISTIVITY METHOD

Prediction of Compressive Strength of Portland Cement Paste Based on Electrical Resistivity Measurement

Continuous Tracking of the Relationship Between Resistivity and Pore Structure of Cement Pastes

Nondestructive Monitoring Hydration of Belite Calcium Sulfoaluminate Cement by EIS Measurement

Using Eccentrically Sample to Find the Relationship Between Resistivity and Cracking Time in Cement Paste Vides Mechanical Strength and Electrical Resistivity

Effect of Temperature on the Electrical Resistivity of Portland Cement Pastes

Study on chemical shrinkage and electrical resistivity of cement pastes at early age

Chemical shrinkage and electrical resistivity of cement at early age