Abstract:CoMoCrSi coatings with different thickness were prepared by high velocity oxy-fuel spraying (HVOF) and atmospheric plasma spraying (APS), respectively. Variation of microstructure and phase constitution the coatings were investigated by SEM and XRD, respectively. Thermal shock performance of the coatings was evaluated by heating (500 °C and 900 °C) and water quenching method. Compared with APS coatings, the as-sprayed HVOF coatings exhibited denser microstructure and higher hardness. The phase and microstructure of the coatings did not change significantly after 50 thermal cycles at 500 °C. On the contrary, spallation was observed in APS coatings with thickness of ∼350 μm during 900 °C thermal shock cycles. Obvious oxidation appeared in all of the coatings after 900 °C thermal shock. Meanwhile, segmentation cracks perpendicular to the coating surface were found in the edge of 900 °C thermal shocked HVOF coatings (both ∼350 μm and ∼130 μm) and APS coatings (∼350 μm). Element interdiffusion was not detected between the substrate and coating after 50 thermal shocks at 900 °C or 500 °C. After the thermal shock at 500 °C, the microhardness of the ∼130 μm coating did not change greatly while the microhardness of the ∼350 μm coating was greatly improved. After the thermal shock at 900 °C, the microhardness of the coating increased by about 40 % due to the reduction of defects in the coating and the generation of hard phases. At the same time, the migration of elements and the oxidation and recrystallization of some phases may increase the hardness of the coating.

Compatibility of low thermal conductivity and high infrared emissivity of plasma-sprayed Sm2Hf2O7 and Pr2Hf2O7 coatings

Phase transformation and thermal conductivity of the APS Y2O3 doped HfO2 coating with hybrid structure

Evolution mechanism of the microstructure and mechanical properties of plasma-sprayed yttria-stabilized hafnia thermal barrier coating at 1400 °C

Plasma sprayed 18mol% YO1.5 stabilized hafnia as potential thermal barrier coating

Infrared radiation and thermal cyclic performance of a high-entropy rare-earth hexaaluminate coating prepared by atmospheric plasma spraying

Properties evaluation and failure behaviour of plasma sprayed Y4Hf3O12 for thermal barrier coating applications

Plasma sprayed Yb4Hf3O12 thermal barrier coatings with excellent thermophysical properties and robust CMAS corrosion resistance

Feasibility research of perovskite‐type PrAlO3+δ as high‐temperature infrared radiation coating

Microstructure and Thermophysical Properties of SrZrO3 Thermal Barrier Coating Prepared by Solution Precursor Plasma Spray

On the Study of Thermal-Sprayed Ni0.2Co0.6Fe0.2CrSi0.2AlTi0.2 HEA Overlay Coating

Thermophysical properties and cyclic lifetime of plasma sprayed SrAl 12 O 19 for thermal barrier coating applications

Plasma Sprayed Ferrite-Based Infrared Radiation Coating Directly from Transition Metal Oxides Without High-Temperature Roasting

Microstructure and thermal shock behavior of CoMoCrSi coatings prepared by HVOF and APS

Elevated-temperature wear behavior and mechanisms of APS-sprayed Al 0.6 TiCrFeCoNi high entropy alloy coating

High-temperature performances of Si-HfO2-based environmental barrier coatings via atmospheric plasma spraying

A promising material for thermal barrier coating: Pyrochlore-related compound Sm 2 FeTaO 7

High-entropy pyrochlores with low thermal conductivity for thermal barrier coating materials

Interfacial Structure and Physical Properties of High-Entropy Oxide Coatings Prepared via Atmospheric Plasma Spraying

High heat flux ablation behaviors of Ir-Hf coatings in wind tunnel tests up to 6.6 MW/m2

Microstructure and Mechanical Property Regulation of Plasma-Sprayed High-Entropy (la0.2nd0.2sm0.2eu0.2gd0.2)2zr2o7 Thick Coatings

Microstructure and Tribological Properties of FeCoCrNi High-Entropy Alloy Coatings Fabricated by Atmospheric Plasma Spraying