Abstract:Ni- or Mn-rich cathode materials have attracted great interest for electric vehicle (EV) applications due to their high gravimetric and volumetric energy densities and low- or cobalt-free compositions. For example, Ni-rich LiNi 1-x Co x/2 Mn x/2 O 2 (NMC) layered cathodes can deliver > 200 mAh/g when they operate at above 4.3 V vs.Li . Cobalt-free LiNi 0.5 Mn 1.5 O 4 (LNMO) spinel operates at around 4.75 V vs.Li and delivers an excellent rate capability due to three-dimensional Li-diffusion pathways in its lattice. However, due to lack of high-voltage stabilities of conventional, carbonate-based electrolytes, such high-voltage operation (> 4.3 V vs.Li ) led to unwanted electrolyte oxidation and simultaneous parasitic reactions occurring at CEI. Different types of cathodes have their own failure mechanisms which are often associated with side reactions occurring at solid-electrolyte interphase (SEI) on graphite anodes. This was possible because the reaction by-products from CEI could migrate and attack SEI layers on anodes. To address the high-voltage related issues, various approaches have been proposed such as tuning chemical compositions of cathode active materials, surface modification of cathodes or anodes, and stabilizing the CEI or SEI using electrolyte additives. In literature, however, there was no single solution that can resolve all the complex issues occurring in the high-voltage battery cells. For example, coated layers on active materials are prone to fail during long-term cycling due to mechanical failure (e.g., crack and pulverization) of active materials. In addition, not only active materials but carbon conductors (e.g., acetylene black) inside a cathode leads to the electrolyte oxidation, prompted by its high electronic conductivity and large surface area. Considering that such parasitic reactions originate from CEI and propagate to anode SEI, there is a dire need of multimodal strategies that can create synergistic effect on stabilizing the electrode-electrolyte interphases in cell level. In this presentation, I will introduce non-conventional strategies that can effectively enhance electrode-electrolyte interphase stabilities and improve full-cell (i.e., using graphite anodes) performances. First, formation of self-healing CEI on cathode active materials will be demonstrated. The interface of LNMO spinel oxide will be passivated by Ti-enriched shell via sacrificial transition metal dissolutions and suppress the side reactions occurring at CEI. Second, a strategy for passivating both cathode active materials and carbon black conductor by using functional binders will be demonstrated. Since the binder coating will be performed in-situ during a slurry preparation, no extra process will be required while implementing this approach to a cell manufacturing. Finally, solid-electrolyte implemented NMC or LNMO cathodes will be demonstrated as an effective approach to stabilize the high-voltage performance by offering good Li-ion conduction pathways at CEI layer. Improvement mechanism of each approach will be also presented based on physical and electrochemical characterization data. Electrochemical impedance spectroscopy (EIS) revealed a suppression of CEI interfacial resistance during cycling, suggesting the enhanced stability of the multifunctional CEI. Various microscopy and spectroscopy data acquired from cycle-aged CEI and graphite SEI will be corelated to the cell performance data and identify the CEI property-performance relationship. These unique multifunction CEI strategies will be applicable to various cathode materials for the next-generation Li-ion batteries. Figure 1

Formation of an Artificial Cathode–Electrolyte Interphase to Suppress Interfacial Degradation of Ni-Rich Cathode Active Material with Sulfide Electrolytes for Solid-State Batteries

Engineering Stable Decomposition Products on Cathode Surfaces to Enable High Voltage All‐Solid‐State Batteries

An Artificial Solid Electrolyte Interphase Enables the Use of a LiNi0.5 Mn1.5 O4 5 V Cathode with Conventional Electrolytes

Organic‐Additive‐Derived Cathode Electrolyte Interphase Layer Mitigating Intertwined Chemical and Mechanical Degradation for Sulfide‐Based Solid‐State Batteries

A Dynamically Stable Sulfide Electrolyte Architecture for High-Performance All-Solid-State Lithium Metal Batteries

A Bifunctional Composite Artificial Solid Electrolyte Interphase for High Stable Solid-State Lithium Batteries

Enhancing Interfacial Stability in Sulfide All-Solid-state Batteries Through Surface Dual-Doping of Zr and F in Ni-rich Cathodes

Enhanced Electrochemical Stability and Extended Cycle Life in Sulfide-Based All-Solid-State Batteries: The Role of Li10 SnP2 S12 Coating on Ni-Rich NCM Cathode

(Invited) Strategies for Enhancing the Stability of the Electrode-Electrolyte Interphase in Sulfide-Based Solid-State Batteries

Slurry-Coated LiNi0.8Co0.1Mn0.1O2-Li3InCl6 Composite Cathode with Enhanced Interfacial Stability for Sulfide-Based All-Solid-State Batteries.

A Plastic-Crystal Electrolyte Layer Promotes Interfacial Stability of Ni-Rich Oxide Cathode in Li6PS5Cl-Based All-Solid-State Rechargeable Li Batteries

Conformal Li 2 HfO 3 /HfO 2 Nanoparticle Coatings on Layered Ni-Rich Oxide Cathodes for Stabilizing Interfaces in All-Solid-State Batteries

An Interphase Engineering Method of Stabilizing Ni‐rich Cathode in Lithium‐ion Batteries by A Nucleophilic‐based Additive

Heuristic Design of Cathode Hybrid Coating for Power‐Limited Sulfide‐Based All‐Solid‐State Lithium Batteries

Designing In-Situ-Formed Interphases Enables Highly Reversible Cobalt-Free LiNiO2 Cathode for Li-ion and Li-metal Batteries

Enabling stable and high-rate cycling of a Ni-rich layered oxide cathode for lithium-ion batteries by modification with an artificial Li<SUP>+</SUP>-conducting cathode-electrolyte interphase

Waxing Bare High-Voltage Cathode Surfaces to Enable Sulfide Solid-State Batteries

(Invited) Non-Conventional, Multimodal Strategies to Create Synergistic Effects on Electrode-Electrolyte Interphase Stabilities in Lithium-Ion Batteries

Toward a High-Voltage Practical Lithium Ion Batteries with Ultraconformal Interphases and Enhanced Battery Safety

Stabilizing Effect of a Hybrid Surface Coating on a Ni-Rich NCM Cathode Material in All-Solid-State Batteries

Chemo-mechanical stable cathode interphase via interface in-situ catalytic-conversion integrated design for all solid-state batteries