Methane Dry Reforming by Ni–Cu Nanoalloys Anchored on Periclase-Phase MgAlO x Nanosheets for Enhanced Syngas Production
Zhourong Xiao,Fang Hou,Junjie Zhang,Qiancheng Zheng,Jisheng Xu,Lun Pan,Li Wang,Jijun Zou,Xiangwen Zhang,Guozhu Li
DOI: https://doi.org/10.1021/acsami.1c14918
2021-10-06
Abstract:Stable and efficient syngas production via methane dry reforming is highly desirable as it utilizes two greenhouse gases simultaneously. In this work, active Ni–Cu nanoalloys stably anchored on periclase-phase MgAlOx nanosheets were successfully synthesized by a hydrothermal method. These highly dispersed small Ni–Cu alloys strongly interacted with the periclase-phase MgAlOx nanosheets, on which abundant base sites were accessible. On the optimal catalyst (6Ni6CuMgAl–S), methane and carbon dioxide conversion always reached 85 and 90% at 700 °C under a gas hour speed velocity of 40,000 mL/gcat h for more than 70 h. The hydrogen production rate was maintained at 1.8 mmol/min, and the ratio of H2/CO was kept at approximately 0.96 under a CH4 and CO2 flow rate of 25 mL/min. Coke deposition and Ni sintering were effectively suppressed by the formation of a Ni–Cu alloy, the laminar structure, and the periclase phase of the MgAlOx support. Moreover, the alloy nanoparticles were reconstructed into a segregated Ni–Cu alloy structure in response to the reaction environment, and this structure was more stable and still active. Density functional theory calculations showed that carbon adsorption was inhibited on the segregated Ni–Cu alloy. Furthermore, the experimental thermogravimetric and O2-TPO results confirmed the significant decrease in carbon deposition on the Ni–Cu alloy catalysts.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c14918.DFT theoretical calculation; additional characterizations of some catalysts, including XRD patterns, SEM images, N2 adsorption, desorption, and pore size distribution; H2-TPR profiles; H2-TPD profiles; HAADF image and element mapping; TEM images; XPS spectra; acid property; and additional reaction data (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology