Preparation of Sba-15 Supported Metals by Vapor-Phase Infiltration

John Vohs,Ching-Yu Wang,Kai Shen,Raymond J. Gorte
DOI: https://doi.org/10.2139/ssrn.4167181
2022-01-01
SSRN Electronic Journal
Abstract:A simple method is presented for incorporating various catalytic metals into the pores of SBA-15 using vapor-phase infiltration. Precursors used in Atomic Layer Deposition (ALD) for Pt, Pd, Rh, Ru, and Ni were exposed to an evacuated SBA-15, resulting in monolayer films of the adsorbed precursors inside the mesopores. The metal particles that formed after removal of the precursor ligands remained in the pores and had particle sizes ranging from 3.8 nm for Pt to 5.2 nm for Ni, as determined by Transmission Electron Microscopy (TEM), XRD, and CO chemisorption. Metal loadings for saturation exposures ranged from 5.1-wt% for Ni to 9.1-wt% for Pt. Control of the metal loading was demonstrated for Pd by varying the amount of precursor that was used. To determine the effect of surface composition of the mesopores, Pd particles were also added to SBA-15 that was coated with a 0.2-nm film of ZrO2.
What problem does this paper attempt to address?