Abstract:TiO2/SBA-15 catalysts, TiO2 nanoparticles well dispersed on SBA-15 supporter, have been successfully obtained through a self-assembly aging, carboxylation and subsequent solvothermal process. Firstly, P123 (PEG-PPG-PEG), KCl, (2-cyanoethyl) triethoxysilane (CETES) and tetraethoxysilane (TEOS) were employed to form cyano-modified SBA-15 (CN/SBA-15) in 2.0 mol/L HCl solution by Self-assembly aging method. Secondly, carboxyl-modified SBA-15 (COOH/SBA-15) was got through carboxylation treatment in 48% H2SO4 solution at 95 degrees C for 24 h. Finally, highly dispersed TiO2/SBA-15 catalysts were successfully synthesized via solvothermal method at 220 degrees C for 12 h using COOH/SBA-15 and tetrabutyl titanate (TB) as raw materials. In order to remove the organic compounds and improve the crystallization of TiO2, the obtained TiO2/SBA-15 catalysts then were filtrated, washed by absolute ethanol for three times, dried at 80 degrees C and calcined at 550 degrees C for 4 h. Notably, the self-assembly and carboxylation process produced large number of good dispersive carboxyl groups (COOH) on SBA-15, which could effectively anchored TB molecules on SBA-15 to promise the highly dispersion of TiO2 on SBA-15. The obtained TiO2/SBA-15 catalysts have been characterized by X-ray diffraction (XRD), Raman spectrum, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), nitrogen adsorption and UV-Visible diffuse reflectance spectroscopy (UV-Vis). Above results indicate that the TiO2/SBA-15 catalysts exhibit large specific surface area and TiO2 on SBA-15 supporter is anatase phase, they are both play important roles in photocatalytic application. In the current manuscript, the photocatalytic reduction of CO2 under UV light irradiation as a prober reaction was used to investigate the photocatalytic performance of TiO2/SBA-15 catalysts. It was found that the obtained catalysts performed high photocatalytic capacity for CO2 reduction, especially when the loading amount of TiO2 was around 16.5 wt% [n(COOH)/n(TB)=3], the methanol production got maximum which could reach 80 mu mol/g-catalyst after 6 h UV light irradiation. Compared with the catalysts which synthesized through simple impregnation method, our TiO2/SBA-15 catalysts showed the higher activity in photocatalytic reduction of CO2, owing to the better dispersion and crystallization.

Preparation of Au/Ti-Sba-15 Catalysts and Their Catalytic Performance for Co Oxidation

Effect of La2O3 Promoter on the Performance of Au/TiO2 Catalyst for Selective Hydrogenation of Cinnamaldehyde

Catalytic Performance of Au III Supported on SiO 2 Modified Activated Carbon

Preparation of Highly Active Silica-Supported Au Catalysts for Co Oxidation by A Solution-Based Technique

High-Surface-Area Mesoporous Crystalline TiO2: Synthesis, Characterization, and Application As Support for Making Stable Au Catalysts

Au/MxOy/TiO2 Catalysts for CO Oxidation: Promotional Effect of Main-Group, Transition, and Rare-Earth Metal Oxide Additives

Novel Au/TiO 2 /al 2 O 3 · X H 2 O Catalysts for CO Oxidation

Heterostructured Catalysts Prepared by Dispersing Au@Fe2O3 Core–shell Structures on Supports and Their Performance in CO Oxidation

Self-assembly of a Highly Stable and Active Co3O4/H-TiO2 Bulk Heterojunction with High-Energy Interfacial Structures for Low Temperature CO Catalytic Oxidation

Synthesis of Supported TiO2/SBA-15 Catalysts and Their Performance on Photocatalytic Reduction of CO2

Active yet extremely durable Co3O4 spheroids of different texture without/with Au deposition for CO oxidation

Pt/MOx/SiO2, Pt/MOx/TiO2, and Pt/MOx/Al2O3 Catalysts for CO Oxidation

Biosynthesized Au/TiO2@SBA-15 Catalysts for Selective Oxidation of Cyclohexane with O-2

Surface Modification of Au/Tio2 Catalysts by Sio2 Via Atomic Layer Deposition

Sintering-resistant and highly active Au/SBA-15 catalyst for carbon monoxide oxidation

Effect of La2O3 on Catalytic Performance of Au/TiO2 for CO Oxidation

CO Preferential Photo-Oxidation in Excess of Hydrogen in Dark and Simulated Solar Light Irradiation over AuCu-Based Catalysts on SBA-15 Mesoporous Silica-Titania

High-Temperature-Stable Au@SnO2 Core/Shell Supported Catalyst for CO Oxidation

Rational Design of Gold Catalysts with Enhanced Thermal Stability: Post Modification of Au/Tio2 by Amorphous Sio2 Decoration

High Activity of Gold/Tin-Dioxide Catalysts for Low-Temperature CO Oxidation: Application of a Reducible Metal Oxide to a Catalyst Support

Rational design of gold catalysts with enhanced thermal stability: post modification of Au/TiO 2 by amorphous SiO 2 decoration