Abstract:Good gas permeability is an essential factor for the smooth operation and high performance in the lower part of the blast furnace. Under the present low carbon blast furnace smelting conditions, the coke layer is thinner, and the proportion of the molten metal in the coke layer is significantly higher, resulting in a major reduction in gas permeability, which seriously affects blast furnace operations. Also, the lower thickness of the coke layer weakens the process of solid-liquid carbon dissolution when the molten iron passes through the coke layer, which reduces the carbon content of the molten iron and further deepens the erosion of the refractory by the unsaturated molten iron. The carbon dissolution in the molten iron in a blast furnace core was measured by a high-temperature vacuum wettability test tool that analyzed the interface wetting activity between Fe−C melts with specific carbon mass fraction (3.8%, 4.3%, 4.8%) and 99.9% of high temperatures graphite plates. Besides, the scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the graphite substrate’s carburizing morphology and carburizing distances. The results show that, with the increase of carbon content, the interface contact angle becomes bigger. The contact angle decreases with time, and eventually reaches a steady-state during the melting process, and the Fe−C melt with saturated carbon cannot be wet. The scanning electron microscopy analysis shows that a spherical cap-like depression is created by a cross-section of the Fe−C melt and the graphite substrate, and the radius and volume of the depression decrease with increasing carbon content. The study of the EDS scanning analysis shows that the amount of dissolved carbon atoms in the graphite substrate penetrates the Fe−C melt and decreases with increasing initial carbon concentration. The smaller the carburizing effect, the better the wetting is conducive to carbon mass transfer. It is found that by measuring carburizing of the carbon atoms in the graphite substrate into the Fe−C melt by calculating the surface energy reduces the surface energy between the two. Thus, the surface tension decreases and the melt spreads slowly with contact angle gradually decreasing during melting.

Softening and melting behaviors of ferrous burden in hydrogen-rich blast furnace cohesive zone

Softening and melting performance of mixed burden under the simulated hydrogen-rich blast furnace atmosphere

Changes in Microscale Liquid Formation in Lump and Sinter Mixed Burden Softening and Melting Tests with the Addition of Hydrogen

Effect of Mixed Charging of Nut Coke and Sinter on Hydrogen-Rich Smelting Process of Blast Furnace

Effect of Hydrogen Addition on Softening and Melting Reduction Behaviors of Ferrous Burden in Gas-Injection Blast Furnace

Relationship and Mechanism Analysis of Soft-Melt Dropping Properties and Primary-Slag Formation Behaviors of the Mixed Burden in Increasing Lump Ore Ratio

Increasing the Softening as well as Melting Behaviors for Iron Ore Materials within the Blast Furnace Cohesive Zone through the High-temperature Interactivity

Review of hydrogen-rich ironmaking technology in blast furnace

Effect of CO–CO2 and H2–H2O on the reduction degree of fluxed pellets: reduction mechanism within hydrogen-rich blast furnace

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Heat distribution model under hydrogen-rich low-carbon conditions in blast furnace

Effect of H2 on Blast Furnace Ironmaking: A Review

Effect of atmosphere and basicity on softening–melting behavior of primary slag formation in cohesive zone

Evolution and process analysis of the hearth activity in hydrogen-rich blast furnace

Effect of Hydrogen-Rich Atmosphere on the Reduction Behavior and Kinetics of Iron-Ore Pellets Under Non-isothermal Conditions

Investigating the Effect of the Iron Ore Pellet Addition on the Interaction Among Blast Furnace Burden in the Cohesive Zone

Effect of Titanomagnetite Ironsand Coal Composite Hot Briquette on Softening-melting Performance of Mixed Burden under Simulated Blast Furnace Conditions

Novel experimental method to simulate reduction behaviour of burden in blast furnace shaft

Non-isothermal Reduction Process Analysis of Iron-Bearing Burden with Charging Iron Coke Hot Briquette under Simulated Blast Furnace Conditions

Numerical Investigation of Burden Distribution in Hydrogen Blast Furnace

Development of softening and melting testing conditions simulating blast furnace operation with hydrogen injection