Abstract:Good gas permeability is an essential factor for the smooth operation and high performance in the lower part of the blast furnace. Under the present low carbon blast furnace smelting conditions, the coke layer is thinner, and the proportion of the molten metal in the coke layer is significantly higher, resulting in a major reduction in gas permeability, which seriously affects blast furnace operations. Also, the lower thickness of the coke layer weakens the process of solid-liquid carbon dissolution when the molten iron passes through the coke layer, which reduces the carbon content of the molten iron and further deepens the erosion of the refractory by the unsaturated molten iron. The carbon dissolution in the molten iron in a blast furnace core was measured by a high-temperature vacuum wettability test tool that analyzed the interface wetting activity between Fe−C melts with specific carbon mass fraction (3.8%, 4.3%, 4.8%) and 99.9% of high temperatures graphite plates. Besides, the scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the graphite substrate’s carburizing morphology and carburizing distances. The results show that, with the increase of carbon content, the interface contact angle becomes bigger. The contact angle decreases with time, and eventually reaches a steady-state during the melting process, and the Fe−C melt with saturated carbon cannot be wet. The scanning electron microscopy analysis shows that a spherical cap-like depression is created by a cross-section of the Fe−C melt and the graphite substrate, and the radius and volume of the depression decrease with increasing carbon content. The study of the EDS scanning analysis shows that the amount of dissolved carbon atoms in the graphite substrate penetrates the Fe−C melt and decreases with increasing initial carbon concentration. The smaller the carburizing effect, the better the wetting is conducive to carbon mass transfer. It is found that by measuring carburizing of the carbon atoms in the graphite substrate into the Fe−C melt by calculating the surface energy reduces the surface energy between the two. Thus, the surface tension decreases and the melt spreads slowly with contact angle gradually decreasing during melting.

Melting–Dropping Property of Blast Furnace Charge on the Basis of its Slag Formation Behavior

Relationship and Mechanism Analysis of Soft-Melt Dropping Properties and Primary-Slag Formation Behaviors of the Mixed Burden in Increasing Lump Ore Ratio

Effect of W(mgo)/w(al2o3) Ratio and Basicity on Microstructure and Metallurgical Properties of Blast Furnace Slag

Evaluating the Effect of MgO/Al2O3 Ratio on Thermal Behaviors and Structures of Blast Furnace Slag with Low Carbon Consumption

Analysis of the melting process of carbon-bearing pellets in iron bath, slag bath and graphite crucible

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Dynamic analysis of liquid permeability in the dripping zone of blast furnace and reaction behavior at the slag-coke interface

Study on the High-Temperature Interaction between Coke and Iron Ores with Different Layer Thicknesses

Quantitative analysis of minerals of blended coal ash at high temperature and its influence on slagging

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Interfacial reaction behavior in blast furnace and analysis of influence mechanism

Numerical Investigation of the Limit of Coke Rate Reduction in an Ironmaking Blast Furnace (BF)

Effect of atmosphere and basicity on softening–melting behavior of primary slag formation in cohesive zone

Softening and melting behaviors of ferrous burden in hydrogen-rich blast furnace cohesive zone

Revealing the Softening-Melting Behaviors and Slag Characteristics of Vanadium-Titanium Magnetite Burden with Various MgO Addition

Novel Blast Furnace Operation Process Involving Charging with Low-Titanium Vanadium–titanium Magnetite Carbon Composite Hot Briquette

Softening–Melting Behaviors of a MgO-SiO2-FeO Slag System on a Coke Bed

Estimation of Iron Ore Pellet Softening in a Blast Furnace with Computational Thermodynamics

Effect of Titanomagnetite Ironsand Coal Composite Hot Briquette on Softening-melting Performance of Mixed Burden under Simulated Blast Furnace Conditions

Influence of Vanadium–Titanium Sinter Basicity on Cohesive Dripping Properties of Blast Furnace Comprehensive Burden

Investigating the Effect of the Iron Ore Pellet Addition on the Interaction Among Blast Furnace Burden in the Cohesive Zone