Influence of Vanadium–Titanium Sinter Basicity on Cohesive Dripping Properties of Blast Furnace Comprehensive Burden

Zhe Ning,Xiyu Wang,Songtao Yang

DOI: https://doi.org/10.3390/min14030293

IF: 2.5

2024-03-12

Minerals

Abstract:Vanadium–titanium ore possesses significant mining and utilization value. The basicity of vanadium–titanium sinter has a direct impact on the formation, location, thickness, permeability, and heat exchange of the cohesive zone in the blast furnace. This paper investigated the influence of increasing the basicity of the sinter on the comprehensive burden's cohesive dripping properties in the blast furnace, while keeping the final slag basicity constant. This study was conducted through cohesive dripping property experiments. The findings indicated that as the sinter basicity in the comprehensive burden structure increased and the corresponding increase in the proportion of pellets occurred, the softening performance of the comprehensive burden improved, the cohesive zone became thinner, the lower edge of the cohesive zone shifted upward, and the softening melting properties became better in general. With an increase in the sinter basicity, the dripping difference pressure of the comprehensive burden decreased, and the dripping rate firstly increased and then decreased. An increase in the sinter basicity of the comprehensive burden structure promoted V reduction, and the V element yield and Cr element yield of the sinter were both increased; the optimal sinter basicity was 2.5, and the corresponding pellet proportion was 42%.

geochemistry & geophysics,mineralogy,mining & mineral processing

What problem does this paper attempt to address?

The paper attempts to address the issue of the impact of the basicity of vanadium-titanium sinter on the cohesive zone dripping performance of the overall burden in the blast furnace smelting process. Specifically, the study explores how adjusting the basicity of the sinter (i.e., the ratio of CaO to SiO₂) and increasing the proportion of pellets affect the formation, location, thickness, permeability, and heat exchange characteristics of the cohesive zone in the blast furnace. The research found that with the increase in sinter basicity, the softening performance of the overall burden improves, the cohesive zone becomes thinner, the lower boundary of the cohesive zone moves upward, and the overall softening and melting performance improves. Additionally, the increase in sinter basicity promotes vanadium reduction, enhancing the yield of vanadium and chromium elements. The study concludes that the optimal sinter basicity is 2.5, with a corresponding pellet proportion of 42%, which has practical significance for production.