Abstract:<p class="a-plus-plus">The high-temperature interactions between vanadium-titanium magnetite carbon composite hot briquettes (VTM-CCBs) and pellets were systematically investigated under simulated blast furnace conditions with respect to the reduction behavior, softening–melting–dripping characteristics, gas permeability, and Ti(C, N) precipitation mechanisms. The results showed that VTM-CCB charging can promote the reduction of the pellet in the packed bed and decrease the compressive strength of the pellet after reduction. The compressive strength of the VTM-CCB after reduction decreased with increasing temperature when the FC/O ratio (the ratio of the fixed carbon mol(C) in coal to the reducible oxygen mol(O) in iron oxides) was higher than 1.0. With an FC/O ratio lower than 1.0, the compressive strength of the VTM-CCB initially decreased and then increased. The FC/O ratio has a significant influence on the softening–melting interaction mechanism between the VTM-CCB and the pellet. With an FC/O ratio of 0.8, the bonding layer at the interface between the pellet and the VTM-CCB (consisting of molten fayalitic slag) can promote the softening process, thereby decreasing the softening start and end temperatures. By increasing the FC/O ratio to 1.4, a dense metallic iron shell with relatively high strength formed at the interface and restricted the collapse of the packed bed, thereby increasing the softening start and end temperatures and ensuring the transport of the reduction gas through the packed bed. The melting point of the primary slag phase increased with increasing FC/O ratio due to a decrease in the FeO content, which resulted in an increase in the melting start temperature from 1273 °C to 1294 °C (1546 K to 1567 K). The gas permeability in the cohesive zone increased with an increasing FC/O ratio of the VTM-CCB due to a combination of the skeletal role performed by the residual VTM-CCB and the decrease in the liquid slag proportion. In addition, as the FC/O ratio increased to 1.4, unconsumed carbon promoted the precipitation of Ti(C, N) at the slag–carbon and slag–metal interfaces, which resulted in a substantial increase in the dripping temperature and deterioration of the dripping behavior of the packed bed. Therefore, to suppress the precipitation of Ti(C, N) and improve the dripping behavior of the packed bed, the FC/O ratio of the charged VTM-CCB should be controlled within an appropriate range.</p>

Effect of Introducing Coke into Ore Layer on Softening-melting-dropping Characteristics of Vanadium-titanium Mixed Burden under Simulating BF Conditions

Interface Behavior and Interaction Mechanism between Vanadium-Titanium Magnetite Carbon Composite Briquette and Sinter in Softening-Melting-Dripping Process

Relationship and Mechanism Analysis of Soft-Melt Dropping Properties and Primary-Slag Formation Behaviors of the Mixed Burden in Increasing Lump Ore Ratio

Softening–melting–dripping characteristics and evolution mechanism of vanadium-bearing titanomagnetite carbon composite briquette used as novel blast furnace burden

Novel Blast Furnace Operation Process Involving Charging with Low-Titanium Vanadium–titanium Magnetite Carbon Composite Hot Briquette

Effect of Titanomagnetite Ironsand Coal Composite Hot Briquette on Softening-melting Performance of Mixed Burden under Simulated Blast Furnace Conditions

Effect of Iron CoKe Hot Briquette on Softening-Melting and Dripping Properties of Blast Furnace Mixed Burden

Revealing the Softening-Melting Behaviors and Slag Characteristics of Vanadium-Titanium Magnetite Burden with Various MgO Addition

Influence of Vanadium–Titanium Sinter Basicity on Cohesive Dripping Properties of Blast Furnace Comprehensive Burden

High-Temperature Interactions Between Vanadium-Titanium Magnetite Carbon Composite Hot Briquettes and Pellets Under Simulated Blast Furnace Conditions

Effect of Mixed Charging of Nut Coke and Sinter on Hydrogen-Rich Smelting Process of Blast Furnace

Effect of MgO content in sinter on the softening–melting behavior of mixed burden made from chromium-bearing vanadium–titanium magnetite

Effect and Function Mechanism of Sinter Basicity on Softening-Melting Behaviors of Mixed Burden Made from Chromium-Bearing Vanadium-Titanium Magnetite

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Study on the High-Temperature Interaction between Coke and Iron Ores with Different Layer Thicknesses

Effect of MgO Addition on the Metallurgical Properties of the Vanadium-Titanium Pellet with Simulating Blast Furnace Conditions

Numerical Investigation of the Limit of Coke Rate Reduction in an Ironmaking Blast Furnace (BF)

Softening–Melting Properties and Slag Evolution of Vanadium Titano-Magnetite Sinter in Hydrogen-Rich Gases

Effect of diboron trioxide on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets

Effect of V2O5 addition on the oxidation induration process of Hongge vanadium titanomagnetite pellet

Interfacial Phenomenon and Marangoni Convection of Fe–C Melt on Coke Substrate under in Situ Observation