Abstract:High purity manganese sulfate(MnSO 4 ) is of great importance due to its applications in lithium-ion batteries, pharmaceutical applications, and within feed additives. As manganese always occurs in combination with iron, laterite and other minerals, co-leaching of Mn and Fe complicates the purification procedure of MnSO 4 . Obtaining high purity MnSO 4 without contamination of calcium and magnesium is difficult, because of their similar chemical properties. Current research involved preparation of highly pure MnSO 4 from low purity MnO 2 . A simple and efficient procedure has been developed for purification of MnSO 4 by using a carbon adsorbent followed by treatment with iminodiacetate functionalised resin polymer. The two-step procedure enabled an extremely pure MnSO 4 generally exceeding 99.9%. Iron has been efficiently removed to below 5 ppm (>99% reduction from ∼1000 ppm), calcium was reduced to ∼100 ppm (>90% reduction from ~1600 ppm) and magnesium was reduced to below 10 ppm (>99% reduction from ~1400 ppm). Adiitionally, simple carbon adsorption effectively reduced lead and zinc to below their detection levels (< 0.050 and 5.00 ppm, respectively) and arsenic was reduced to below its level of quantification (< 0.375 ppm). Careful adaptation of the procedure allows for producing high purity manganese salts at a larger scale. Le sulfate de manganèse d'une grande pureté est d'une grande importance en raison de ses applications dans les batteries aux ions de lithium, de ses applications pharmaceutiques et comme additifs alimentaires. Les minerais de manganèse de haute qualité tels que la pyrolusite (MnO 2 , 63.2% Mn) sont appauvris, et les minerais de Fe-Mn tels que le mica ferromagnésien (K(Mg,Fe) 3 (AlSi 3 O 10 )(F,OH) 2 ) deviennent des ressources importantes pour l'extraction du manganèse. Comme le manganèse se trouve toujours en combinaison avec du fer, de la latérite et d'autres minéraux, la co-lixiviation du Mn et du Fe complique la procédure de purification du sulfate de manganèse. Obtenir du MnSO 4 d'une grande pureté sans contamination par le Ca et le Mg est difficile en raison de leurs propriétés chimiques similaires. Les recherches courantes impliquaient la préparation de sulfate de manganèse très pur à partir de bioxyde de manganèse de basse pureté. On a développé une procédure de traitement simple et efficace pour la purification du sulfate de manganèse en utilisant en utilisant un adsorbant au carbone suivi d'un traitement avec un polymère de résine fonctionnalisé par l'iminodiacétate. La procédure en deux étapes a permis d'obtenir un sulfate de manganèse extrêmement pur généralement supérieur à 99.9% et le fer a été éliminé efficacement à moins de 5 ppm (> 99% de sa teneur initiale ∼1000 ppm). Avec ce procédé, le calcium était réduit à environ 100 ppm (> 90%) par rapport à sa teneur initiale d'environ 1600 ppm et le magnésium était réduit à moins de 10 ppm (> 99%) par rapport à sa teneur initiale d'environ 1400 ppm. De plus, simplement en utilisant la technique d'adsorption, on a réduit les impuretés élémentaires de Pb et de Zn en dessous de leurs niveaux de détection (< 0.050, 5.00 ppm, respectivement), et As était réduit en dessous de son niveau de quantification (< 0.375 ppm). Une adaptation attentive de la procédure peut être d'une grande importance pour permettre la production à plus grande échelle des sels de manganèse d'une grande pureté.

Preparation of Magnesium Chloride from Magnesite Dust Using Hydrochloric Acid Leaching and Spray Drying

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Magnesium Chloride Crystals with Studying Mechanism and Leaching Kinetics of Serpentinite Ore by Hydrochloric Acid

Research on preparation of high purity magnesite from MgCl2·6H2O

Study on the Recovery of Magnesium Sulfate Heptahydrate from Brine Sludge Produced in Soda Industry

Study on magnesium reduction process for air-cooled high magnesium-bearing blast furnace slag

Recovery of Mg from H2SO4 Leaching Solution of Serpentine to Precipitation of High-Purity Mg(OH)2 and 4MgCO3·Mg(OH)2·4H2O

Comprehensive Use of Dolomite-Talc Ore to Prepare Talc, Nano-Mgo and Lightweight CaCO3 Using an Acid Leaching Method

Recovery of Magnesium from Ferronickel Slag to Prepare Hydrated Magnesium Sulfate by Hydrometallurgy Method

Using Magnesium Chloride to Volatilize Impurity Metals from Waste Magnesia–Chromium Refractories

Preparation of Carnallite and Magnesium Sulfate from Refined Magnesium Slag

Study on Removal of Calcium and Magnesium from Leaching Solution of Manganese Ore by Solvent Extraction

Study on the Recovery of Flake Magnesium Hydroxide from Brine Sludge in Soda Industry

Preparation of Low-Cost Magnesium Oxychloride Cement Using Magnesium Residue Byproducts from the Production of Lithium Carbonate from Salt Lakes

Preparation of High-Purity Ultrafine Magnesium Hydroxide Using Solid-State Reaction Method

The Efficient Removal of Calcium and Magnesium Ions from Industrial Manganese Sulfate Solution Through the Integrated Application of Concentrated Sulfuric Acid and Ethanol

Technology for obtaining high-pure magnesium compounds using the hydrolytic processes of sedimentation

Magnesium extraction of ferronickel slag processed by alkali fusion and hydrochloric acid leaching

Preparation of high-purity manganese sulfate and removal of unwanted metal ions using resin-based purification

Extraction of magnesium from mine tailings for carbon dioxide mineralization: A preliminary study of the effect of ammonium sulfate to tailings ratio on products and yield

Preparation of Ccalcining MgO and its precursor