Abstract:Expanded graphite has promising potential environmental applications due to its porous structure and oleophilic nature, which allow it to absorb large quantities of oil. The material is produced by intercalating graphite and applying heat to convert the intercalant into gas to cause expansion between the layers in the graphite. Using different intercalants and temperature conditions results in varying properties of expanded graphite. This work has proven that the sorption properties of commercial expanded graphite differ significantly due to the material's structural and elemental characteristics, which can be attributed to the intercalation method. This resulted in various degrees of exfoliation of the graphite and possible functionalisation of the graphene sheets within the structure. This affected the material's sorption capacity and its affinity for heavy metal sorption by incorporating selectivity towards the sorption of certain metals. It was found that sample EG3, which underwent a less harsh expansion, exhibited lower porosity than EG1, and thus, the sample absorbed less oil at 37.29 g/g compared to the more expanded samples EG1 and EG2 with 55.16 g/g and 48.82 g/g, respectively. However, it was able to entrap a wider variety of metal particles compared to EG1 and EG2, possibly due to its smaller cavities allowing for a capillary effect between the graphene sheets and greater Van der Waals forces. A second possibility is that ionic or coordination complexes could form with certain metals due to the possible functionalisation of the expanded graphite during the intercalation process. This would be in addition to coordination between the metals and expanded graphite carbon atoms. The findings suggest that there is evidence of functionalisation as determined by XRD and elemental analyses. However, further investigation is necessary to confirm this hypothesis. The findings in this work suggest that the first mechanism of sorption was more likely to be related to the degree of expansion of the expanded graphite. Various metals are present in used oil, and their removal can be challenging. Some metals in oil are not considered heavy since they have a relatively low density but can be associated with heavy metals in terms of toxicity.

Adsorption effect of added powder graphite on reduction of volatile organic compounds emissions from expanded polystyrene

Change in Conductive-Radiative Heat Transfer Mechanism Forced by Graphite Microfiller in Expanded Polystyrene Thermal Insulation-Experimental and Simulated Investigations

Improving the fire performance and smoke suppression of expandable polystyrene foams by coating with multi‐dimensional carbon nanoparticles

Change in the Properties of Expanded Polystyrene Exposed to Solar Radiation in Real Aging Conditions

Optimizing the Composition Design of Cement-Based Expanded-Polystyrene (EPS) Exterior Wall Based on Thermal Insulation and Flame Retardance

Preparation of recycled graphite/expanded polystyrene by a facile solvent dissolution method

Small-scale experimental study on EPS ETICS and flame-retardant coating reaction-to-fire performance

Combustion characteristics and fire hazard of polystyrene exterior wall thermal insulation materials

Evaluating the Effectiveness of Cellulose-Based Surfactants in Expandable Graphite Wood Coatings

The Effect of Intumescent Coating Containing Expandable Graphite onto Spruce Wood

A Comparative Study of the Effect of Multidimensional Carbon Fillers on Polystyrene Using Supercritical Carbon Dioxide Foaming

VOC Emission from Lightweight Wood Fiber Insulation Board

Novel preparation method and fire performance study of EPS composites based on calcium sulphate hemihydrate

A facile and efficient flame-retardant and smoke-suppressant resin coating for expanded polystyrene foams

Graphite oxide, graphene, and metal-loaded graphene for fire safety applications of polystyrene

Experimental Study on the Surface Pyrolysis Properties and Modeling of Expanded Polystyrene

Covalent modification of graphene oxide and applications in polystyrene composites

Effects of expanded graphite's structural and elemental characteristics on its oil and heavy metal sorption properties

A Porous Carbon with Excellent Gas Storage Properties from Waste Polystyrene

Gypsum Composites with Modified Waste Expanded Polystyrene

Fire safety evaluation of expanded polystyrene foam by multi-scale methods