Abstract:The relatively low hydrothermal stability of Al-rich Cu-SSZ-13 catalysts hinders their practical application in ammonia selective catalytic reduction (NH3-SCR) reaction. Rare-earth ions were introduced into the Al-rich SSZ-13 zeolite using an organotemplate-free synthesis prior to the exchange of Cu2+ ions. Among the rare-earth ions tested (Ce, La, Sm, Y, Yb), Y shows significant enhancement of the hydrothermal stability and NH3-SCR activities after severe hydrothermal aging at 800 degrees C for 16 h when compared with Cu-SSZ-13 without Y. Cu-Y-SSZ-13 catalysts with various amounts of Y were prepared, and it is found that with increasing Y content, the low temperature NO conversions can be improved even after hydrothermal aging. SEM-EDX analysis together with two-dimensional multiple quantum magic-angle-spinning nuclear magnetic resonance (Na-23 MQ MAS NMR) confirms that the Y ions are successfully incorporated into the ion-exchange sites of the SSZ-13 zeolite. Results from Al-27 MAS, Si-29 MAS NMR, temperature-programmed desorption of ammonia (NH3-TPD) and quantitative H-1 MAS NMR indicate that Y can stabilize the framework Al and also preserve the BrOnsted acid sites in the Al-rich SSZ-13 zeolite. The hydrogen temperature programmed reduction (H-2-TPR), ultraviolet-visible-near infrared spectroscopy (UV-vis-NIR) and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) of nitric oxide (NO) or NH3 adsorption demonstrate that introduction of Y ions causes Cu2+ ions to preferentially occupy the 6-MR, which has high hydrothermal stability. However, too much of Y may lead to activity loss at both low and high temperatures. The optimized Al-rich Cu-Y-SSZ-13 with 2.8 wt% of copper (Cu) and 1.3 wt% of Y displays almost the same deNO(x) activities as the conventional organotemplated high silica Cu-SSZ-13 catalyst in a wide reaction temperature window of 150-650 degrees C after severe hydrothermal treatment. Rare-earth ions could be an effective additive for Cu-SSZ-13 catalysts to further improve their hydrothermal stability for practical applications.

Effect of the Preparation Method on the Catalytic Properties of Copper-containing Zeolite Y Applied for NH3-SCR-DeNOx

catalysts Experimental and Theoretical Studies of Sonically Prepared Cu–Y, Cu–USY and Cu–ZSM-5 Catalysts for SCR deNO x

Characterization of Commercial Cu-SSZ-13 and Cu-SAPO-34 Catalysts with Hydrothermal Treatment for NH3-SCR of NOx in Diesel Exhaust

Disclosing the enhanced NH3-SCR-DeNO activity of Cu-containing zeolite Y prepared with 15-Crown-5

Rare-earth ion exchanged Cu-SSZ-13 zeolite from organotemplate-free synthesis with enhanced hydrothermal stability in NH3-SCR of NOx

Understanding enhancement of strong Copper-Yttrium interactions on catalytic properties of Cu/Y-SSZ-13 for NH 3 -SCR

Understanding Enhancement of Strong Copper-Yttrium Interactions on Catalytic Properties of Cu/Y-SSZ-13 for NH3-SCR

Rare‐earth Yttrium Exchanged Cu‐SSZ‐39 Zeolite with Superior Hydrothermal Stability and SO2‐Tolerance in NH3‐SCR of NOx

Selective Catalytic Reduction of NOx with Ammonia over Copper Ion Exchanged SAPO‐47 Zeolites in a Wide Temperature Range

Selective catalytic reduction of nitrogen oxides over a modified silicoaluminophosphate commercial zeolite

Effect of Cu loading content on the catalytic performance of Cu-USY catalysts for selective catalytic reduction of NO with NH3

Effect of Ion-Exchange Sequences on Catalytic Performance of Cerium-Modified Cu-SSZ-13 Catalysts for NH3-SCR

Unraveling the NH3-SCR-DeNOx Mechanism of Cu-SSZ-13 Variants by Spectroscopic and Transient Techniques

Cu, Co, or Ni species in exchanged Y zeolite catalysts and their denitration performance for selective catalytic reduction by ammonia

On the performance of Fe-Cu-ZSM-5 catalyst for the selective catalytic reduction of NO with NH3: the influence of preparation method

Effect of the preparation method on activity of Cu-ZSM-5 nanocatalyst for the selective reduction of NO by NH3

Catalytic Performances of Cu/MCM-22 Zeolites with Different Cu Loadings in NH3-SCR

Progress for Cu-based Small Pore Molecular Sieves As Disel De-NOx Catalysts

Optimization of isolated copper species on the NH 3 -SCR performance over Cu/SSZ-39 modified by ammonia water

Self-synthesis and performance analysis of a Cu-Fe composite ZSM-5 zeolitic catalyst for NOx reduction and particulate matter removal using NH3 SCR

Supercritical Ion Exchange: A New Player in Cu-Zeolite Catalyst Synthesis Towards NH 3 -SCR of NOx