Abstract:Steel-basalt hybrid fibers reinforced cementitious composite (SBFRCC) is a potential reinforce-ment and repair material for engineering structures with fire risk due to its excellent mechanical properties exposed to ambient and high temperatures. However, the bonding properties between SBFRCC and existing concrete are still unclear, especially at high temperatures. To fill this gap, the bonding properties between SBFRCC and existing concrete at high temperatures were investigated based on two situations by using the slant shear and splitting tensile tests. First, the existing concrete was heated at high temperatures and then bonded with SBFRCC and strengthening concrete to form combined systems, respectively. The effects of the interface roughness, high temperature duration, and post-fire-curing on their bonding properties were investigated. Second, the existing concrete was bonded with SBFRCC and then heated at high temperatures, and the effects of fly ash substation rates on the bonding properties were studied. Besides, the backscattered-electron (BSE) was used to observe the interface between the exiting concrete and SBFRCC exposed to various temperatures. Results show that the first bonded and then heated specimens are slide-failed and separated at the bonding interface from room tem-perature to 600 degrees C, while the damage is generated within the existing concrete at 800 degrees C. SBFRCC has better high temperature resistance than the existing concrete. The slant shear and splitting tensile strengths between PC-A and SBFRCC are 9%-33.3% higher than that of PC-A and strengthening concrete at all temperatures. The appropriate roughness at the interface by pol-ishing can significantly improve the bonding properties between the existing concrete and SBFRCC. The bonding strength is recovered by more than 18.2% and 29.8% after the post-fire curing of 28 and 90 d, respectively. The increase of fly ash substitution rates has a certain contribution to the bonding properties above 600 degrees C.

Effect of ground granulated blast furnace slag on the properties of hybrid‐fiber‐reinforced high‐strength concrete under normal and high temperatures

Flexural properties after exposure to elevated temperatures of a ground granulated blast furnace slag concrete incorporating steel fibers and polypropylene fibers

Mechanical Properties of HPC Incorporating Fly Ash and Ground Granulated Blast Furnace Slag After Exposure to High Temperatures

Effects of Fly Ash and Ground Granulated Blast-Furnaces Slag on Properties of High-Strength Concrete

Bonding Properties Between Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites and Existing Concrete at High Temperatures

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Effect of Carbon Fiber on Mechanical Properties and Dimensional Stability of Concrete Incorporated with Granulated-Blast Furnace Slag

Effect of High-Temperature Curing Methods on the Compressive Strength Development of Concrete Containing High Volumes of Ground Granulated Blast-Furnace Slag

Compressive Strength and Microstructural Development of Cementitious Mixtures Incorporating Ultrafine Granulated Blast Furnace Slag

Splitting Strength of Ggbfs Concrete Incorporating with Steel Fiber and Polypropylene Fiber after Exposure to Elevated Temperatures

Property Assessment of High-Performance Concrete Containing Three Types of Fibers

Mechanical properties and corrosion resistance of high performance fiber-reinforced concrete with steel or amorphous alloy fibers

Mechanical Properties of Hybrid Steel-Polypropylene Fiber Reinforced High Strength Concrete Exposed to Various Temperatures

Mass GGBFS Concrete Mixed with Recycled Aggregates as Alkali-Active Substances: Workability, Temperature History and Strength

Effects of hybrid fibers on properties of desulfurized gypsum-based composite cementitious materials

Synergistic effects of hybrid microfibers on mechanical, thermal, and microstructural characterization of nanocomposites

Evaluation of the long-term performance of high-performance concrete produced with blended river sand/sea sand and high-volume GGBFS

Effects of aircraft operating fluids and environmental thermal fatigue on fly ash and steel slag based cementitious composites

Mechanical Properties and Chloride Penetration Resistance of Concrete Combined with Ground Granulate Blast Furnace Slag and Macro Synthetic Fiber

Mechanical and fracture characteristics of ultra-high performance concretes reinforced with hybridization of steel and glass fibers