Abstract:As the main gel material of concrete, cement is used in an astonishing amount every year in the construction industry. However, a large amount of CO 2 is emitted into the atmosphere while producing cement. Therefore, it is the general trend to look for substitutes for cement and develop new green concrete. Lithium slag (LS) is the industrial waste discharged from lithium salt plants. Through testing, it is found that the chemical composition of LS has a high degree of coincidence with ordinary Portland cement (OPC) Therefore, LS can be incorporated into concrete as supplementary cementations material (SCM) to prepare lithium slag concrete (LSC). The pollution of the natural environment caused by a large number of piled-up and landfilled LS is immeasurable. Consuming and using LS in large quantities and with high efficiency not only eliminates the pollution of lithium slag to the natural environment, but also helps to reduce the amount of cement used in green concrete and truly reuse waste resources. In order to study the mechanical properties of post-heated LSC, the test were carried out for LSC specimens after high-temperature. The main influence factors were considered, including the temperatures of 20°C, 100 °C, 300 °C, 500 °C and 700 °C, the contents of lithium slag in LSC of 0%, 10%, 20% and 30%, cooling method of LSC after exposure high temperature. The results showed that the mechanical properties of LS concrete specimens were slightly improved at 100 °C, and when the temperature was 300 °C or higher, the damage to the specimens was huge and irreversible. An appropriate amount of LS (20% lithium slag content) could improve the strength of LSC. This paper also studied the relationship between lithium slag content and strengths of LS concrete. The research results show that adding an appropriate amount of LS to concrete improves the mechanical properties of concrete. When the LS replacement rate is 20%, the mass loss rate of LSC after different high temperature treatments was the minimum. The cubic compressive strength, axial compressive strength, and flexural strength of specimens with 20% LS substitution can be increased by 8.16%, 8.33%, and 13.46% after high temperature. The cubic compressive strength, axial compressive strength, and flexural strength of specimens with 20% LS substitution can be increased by 8.16%, 8.33%, and 13.46% after high temperature.

What problem does this paper attempt to address?

The paper primarily explores the impact of high temperatures on the mechanical properties of Lithium Slag Concrete (LSC). Specifically, the study focuses on the following aspects: 1. **Background and Motivation**: Given the negative environmental impact caused by the large amount of carbon dioxide emissions during cement production, finding alternatives to cement to develop new green concrete has become an important research direction. Lithium slag (LS), as an industrial waste, has been found to be highly similar to Ordinary Portland Cement (OPC) in terms of chemical composition, making it a potential partial replacement material for cement. 2. **Research Objectives**: Through experiments, the study investigates the effects of different temperatures (20°C, 100°C, 300°C, 500°C, and 700°C), different lithium slag contents (0%, 10%, 20%, and 30%), and different cooling methods (Natural Cooling, NC and Water Spray Cooling, WSC) on the mechanical properties of lithium slag concrete. 3. **Main Findings**: - At 100°C, the mechanical properties of lithium slag concrete slightly improve. - When the temperature reaches 300°C or higher, the damage to the samples is significant and irreversible. - Adding an appropriate amount of lithium slag (20% lithium slag content) can enhance the strength of lithium slag concrete. - The study also explores the relationship between lithium slag content and the strength of lithium slag concrete. - When the lithium slag replacement rate is 20%, the mass loss rate of lithium slag concrete after different high-temperature treatments is minimal. - With a 20% lithium slag replacement rate, the compressive strength of the cube, axial compressive strength, and flexural strength after high-temperature treatment increased by 8.16%, 8.33%, and 13.46%, respectively. In summary, this paper aims to evaluate the mechanical properties of lithium slag concrete under high-temperature conditions and to explore the effects of lithium slag content and cooling methods on its performance. The research results indicate that appropriately adding lithium slag can improve the performance of concrete, especially at a 20% replacement rate. This provides experimental evidence and technical support for using lithium slag as a green building material.

Effect of high temperature on mechanical properties of lithium slag concrete

Research on the High Performance of Concrete Mixed with Lithium Slag in Hydraulic Structures

Fresh, mechanical, and microstructural properties of lithium slag concretes

Experimental Study on High-performance Lithium Slag Concrete

Compression stress-strain curve of lithium slag recycled fine aggregate concrete

Research on pore structure parameters and activity of lithium slag concrete

Improving the post-fire behaviour of steel slag coarse aggregate concrete by adding GGBFS

Axial compression stress-strain relationship of lithium slag rubber concrete

Revisiting the Effect of Slag in Reducing Heat of Hydration in Concrete in Comparison to Other Supplementary Cementitious Materials

Effects of Lithium Slag on the Frost Resistance of Cement-Soil

The Permeability of Resistance to Chloride Ion of High Performance Concrete with Lithium Slag and Steel Slag

Research on strength and microscopic characteristics of lime-activated fly ash-slag solidified sludge under high temperature effect

Research Progress on the Activity Stimulation of Lithium Slag in Concrete

Enhancing the post-fire behavior of steel slag normal-strength concrete by adding SCM

Effect of Mineral-Generated Lithium Slag on the Properties of Magnesium Oxychloride Cement

Modification of ultrafine blast furnace slag with steel slag as a novel high-quality mineral admixture to prepare high-strength concrete

The Influence of Slag Content on the Structure and Properties of the Interfacial Transition Zone of Ceramisite Lightweight Aggregate Concrete

Feasibility of Waste Foundry Sand in High-Strength Self-Compacting Concrete and the Effects of Elevated Temperatures

Effect of Lithium Slag on Drying Shrinkage of Concrete with Manufactured-sand

Experimental Study Based on Box–Behnken Design and Response Surface Methodology for Optimization Proportioning of Activated Lithium Slag Composite Cement-Based Cementitious Materials

Effect of the Curing Condition and High-Temperature Exposure on Ground-Granulated Blast-Furnace Slag Cement Concrete