Abstract:As the main gel material of concrete, cement is used in an astonishing amount every year in the construction industry. However, a large amount of CO 2 is emitted into the atmosphere while producing cement. Therefore, it is the general trend to look for substitutes for cement and develop new green concrete. Lithium slag (LS) is the industrial waste discharged from lithium salt plants. Through testing, it is found that the chemical composition of LS has a high degree of coincidence with ordinary Portland cement (OPC) Therefore, LS can be incorporated into concrete as supplementary cementations material (SCM) to prepare lithium slag concrete (LSC). The pollution of the natural environment caused by a large number of piled-up and landfilled LS is immeasurable. Consuming and using LS in large quantities and with high efficiency not only eliminates the pollution of lithium slag to the natural environment, but also helps to reduce the amount of cement used in green concrete and truly reuse waste resources. In order to study the mechanical properties of post-heated LSC, the test were carried out for LSC specimens after high-temperature. The main influence factors were considered, including the temperatures of 20°C, 100 °C, 300 °C, 500 °C and 700 °C, the contents of lithium slag in LSC of 0%, 10%, 20% and 30%, cooling method of LSC after exposure high temperature. The results showed that the mechanical properties of LS concrete specimens were slightly improved at 100 °C, and when the temperature was 300 °C or higher, the damage to the specimens was huge and irreversible. An appropriate amount of LS (20% lithium slag content) could improve the strength of LSC. This paper also studied the relationship between lithium slag content and strengths of LS concrete. The research results show that adding an appropriate amount of LS to concrete improves the mechanical properties of concrete. When the LS replacement rate is 20%, the mass loss rate of LSC after different high temperature treatments was the minimum. The cubic compressive strength, axial compressive strength, and flexural strength of specimens with 20% LS substitution can be increased by 8.16%, 8.33%, and 13.46% after high temperature. The cubic compressive strength, axial compressive strength, and flexural strength of specimens with 20% LS substitution can be increased by 8.16%, 8.33%, and 13.46% after high temperature.

Improving the post-fire behaviour of steel slag coarse aggregate concrete by adding GGBFS

Enhancing the post-fire behavior of steel slag normal-strength concrete by adding SCM

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

Mechanical performance, microstructure, and damage model of concrete containing steel slag aggregate

Bonding Properties Between Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites and Existing Concrete at High Temperatures

Experimental study on strength and abrasion-resistance enhancement admixture

Preparation and Hydration Properties of Steel Slag-Based Composite Cementitious Materials with High Strength

Flexural properties after exposure to elevated temperatures of a ground granulated blast furnace slag concrete incorporating steel fibers and polypropylene fibers

Durability and mechanical behaviors of steel slag powder concrete

Enhancement of ultra-fine slag on compressive strength of solid waste-based cementitious materials: Towards low carbon emissions

Study on Road Performance of Cement Fly Ash Stabilized Steel Slag-Concrete Recycled Macadam

Recycle of steel slag as cementitious material and fine aggregate in concrete: mechanical, durability property and environmental impact

A multi-scale experimental investigation of the feasibility of using integrated coal gasification combined slag as a supplementary cementitious material

Effect of high temperature on mechanical properties of lithium slag concrete

Recycling of steel slag powder in green ultra-high strength concrete (UHSC) mortar at various curing conditions

Effect of Steel Slag Aggregate on Pavement and Flame-Retardant Performance of Warm-Mixed Flame-Retardant Asphalt Concrete

Compressive behavior of steel slag fine aggregate concrete under impact loading

Hydration Superposition Effect and Mechanism of Steel Slag Powder and Granulated Blast Furnace Slag Powder

Feasibility of Waste Foundry Sand in High-Strength Self-Compacting Concrete and the Effects of Elevated Temperatures

High-temperature modification of steel slag using composite modifier containing silicon calcium slag, fly ash, and reservoir sediment