Abstract:A blast furnace operates under a countercurrent flow process, and a wide variety of physical and chemical reactions take place, especially in the hearth at the highest temperature. Therefore, the working status and erosion of the carbon brick have a critical influence on the longevity of the blast furnace. Although the phenomena in the hearth cannot be directly observed through the black box, hearth dissection provides an alternative way to access and subsequently evaluate the internal conditions. In this paper, a 4000 m3 blast furnace hearth was dissected, and 12 residual iron samples were collected and subjected to composition, morphology, and thermal conductivity analyses. The results show that in the center of the hearth, the residual iron had thicker metallic iron strips. This is because the residual iron in the center of the dissected hearth was fully mixed with carbon or coke, and this mixing apparently enhanced the heat conductivity in the center of the hearth to as great as 80.5 W/(m K). However, such a mixing state was gradually relieved in the regions either close to the wall or settling on the bottom. Thus, the residual iron near the wall formed a needle-like surface with a layer-by-layer structure in the form of alternatively thinner strip-shaped carbon and metallic iron, and the thermal conductivities of the residual iron near the wall were above 40.0 W/(m K) regardless of the relative height. Moreover, the erosion mechanisms of the blast furnace hearth wall are proposed, and the erosion thickness is accordingly evaluated based on the heat transfer model, in which the measured thermal conductivities of the residual iron are taken into consideration. According to the erosion mechanism, the thickness of residual iron is thinner, the erosion is more serious.

Consideration of long campaign based on analysis of 4038 m3 blast-furnace hearth core investigation

Influence of the Residual Iron on the Erosion of Carbon Bricks in a 4000 m3 Blast Furnace Hearth: From the Measured Properties to the Proposed Mechanisms

Erosion Mechanism of Carbon Brick in Hearth of 4000 m3 Industrial Blast Furnace

Investigation of the Hearth Erosion of WISCO No. 1 Blast Furnace Based on the Numerical Analysis of Iron Flow and Heat Transfer in the Hearth

Occurrence State and Behavior of Carbon Brick Brittle in a Large Dissected Blast Furnace Hearth

Migration Behavior of K, Na, S, Ti in Hearth of a Commercial Blast Furnace

Heat Transfer Evolution Process in Hearth Based on Blast Furnace Dissection

Thermal Stress Analysis of Blast Furnace Hearth with Typical Erosion Based on Thermal Fluid-Solid Coupling

Erosion Behavior and Longevity Technologies of Refractory Linings in Blast Furnaces for Ironmaking: A Review

A Preliminary Model for Liquid Solidification in Blast Furnace Hearth

Analysis of the Relationship between Productivity and Hearth Wall Temperature of a Commercial Blast Furnace and Model Prediction

Formation mechanism of the brittle layer in carbon brick of blast furnace hearth

Study on Corrosion Resistance of S-Carbon Bricks for Blast Furnace Hearth in Molten Iron

Numerical Simulation of Blast Furnace Hearth Maintenance Measures

Numerical Modeling of Multiphase Flow,heat Transfer and Titanium Flow Behavior in Blast Furnace Hearth

Technological Measures for Prolonging Hearth Life of Blast Furnace

Numerical Simulation Model for Evaluating Protection Measures of Blast Furnace Hearth

A Model to Simulate Titanium Behavior in the Iron Blast Furnace Hearth

Estimation of the Blast Furnace Hearth State Using an Inverse-Problem-Based Wear Model

Numerical Analysis of Titanium Compounds in Blast Furnace Hearth During Titania Addition

Numerical Analysis on Erosion and Optimization of a Blast Furnace Main Trough