Abstract:Abstract Aluminum can enhance heat release of energetic composite in theory. However, the commonly used micron aluminum powder has several short comings like incomplete reaction and low reaction rate. Meanwhile, outer oxide shell of nano Al particle is thicker than micro Al, which leads to low active aluminum content and insufficient heat release. On the basis of previous research, reported fluoropolymers modified Al particles were compared and suitable F2311was chosen. Sub-micron scale Al (median particle size around 200 nm) was regarded as optimum coated object in consideration of activity content of aluminum powder changing with particle size. The super fine Al powder was prepared by electrical explosion method, and encapsulated in situ by selected fluorine rubber F2311. The experiments on thermal stability demonstrated F2311 coating thickness should be no less than 3.6 nm. These results were further confirmed by EXPLO5 thermo dynamic calculation. Calculated results showed that reaction characters of F2311 encapsulated Al exceeded conventional nano Al regardless of combustion and explosion. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), laser particle size analyzer and X-ray photoelectron spectroscopy (XPS) were used to characterize coated products’ morphology, particle size distribution and interfacial bonding information. The results showed that the coated samples were generally spherical shape, with median particle size of 217.7 nm and coating thickness of 3.6 nm. The coating shell contained a small amount of alumina and aluminum fluoride besides fluoropolymer. The non-isothermal dynamic equations of Al/F2311 and Al/Al 2 O 3 were deduced by TG/DSC simultaneous thermal analysis. Compared with conventional nano-Al, the apparent activation energy of Al/F2311 decreased by 45 kJ/mol and the first exothermic peak temperature was about 10 °C earlier. Moreover, heat release was nearly twice as conventional nano-Al. TG-DSC-MS coupled measurements certified that active Al was enveloped by ‘fluorine atmosphere’ while F2311 decomposed in range of 200–400 °C. Alumina was replaced with aluminum fluoride inside coating layer during 400–550 °C, which broadened the diffusion path and then accelerated the permeation of oxidizing gas. In addition, the exothermic of Al-F was obviously larger than Al-O. Consequently, the oxidation reaction was activated rapidly, especially in initial exothermic period. Fluoropolymer encapsulated sub-micron sized Al was a latent highly activity energetic fuel and a potential candidate for aluminum powder.

Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder

Core-shell particle of aluminum-copper perfluorooctanoate configurations and its ignition and combustion properties

In situ preparation of Al@3-Perfluorohexyl-1, 2-epoxypropane@glycidyl azide polymer (Al@PFHP@GAP) high-energy material

Preparation of core-shell structured Al-5Li@HTPB powders with improved stability and combustion performance by using perfluoroalkylsilane as a surfactant

Enhanced combustion performance of core-shell aluminum with poly(vinylidene fluoride) interfacial layer: Constructing the combination bridge of aluminum powder and poly(vinylidene fluoride)

Core-shell Structured Nal@f-X Nanocomposite: Preparation and Their Improved Combustion Performances

Improved ignition and combustion performances of aluminum nanoparticles by in-situ partial conversion of native alumina to surface Al-MOF shell

High Performance Nal@cuo Core-Shell Particles with Improved Combustion Efficiency and the Effect of Interfacial Layers on Combustion

Preparation of high-energy Al-Li alloy powders with enhanced compatibility and combustion performance by dense fluorosilane polymer composite coating

Enhancing the combustion of nAl with AlF 3 coating: gas–solid reaction mechanism for reducing combustion agglomeration of Al powder

Polyphenols-inspired interface modification and reduced agglomeration of solid propellants via a functionalized fluorine-containing organic substance coating layer

Ignition and Combustion Characteristics of Aluminum-Based Fluorine-Containing Composite Powder

Tuning the Reactivity of Perfluoropolyether-Functionalized Aluminum Nanoparticles by the Reaction Interface Fuel-Oxidizer Ratio

THERMAL REACTIVITY OF AL/FE CORE−SHELL NANOCOMPOSITES

Calcium Fluoride Promoting the Combustion of Aluminum Powder

Optimization effect and reaction mechanism of flake aluminum powder on the combustion performance of high-energy-density JP-10/PO composite fuel

Facile solvent evaporation synthesis of core-shell structured Al@PVDF nanoparticles with excellent corrosion resistance and combustion properties

Improvement of ignition and combustion performance of micro-aluminum particles by double-shell nickel-phosphorus alloy coating

The combustion-supporting mechanism of fluoropolymer on aluminum particles using reactive dynamics simulations

A latent highly activity energetic fuel: thermal stability and interfacial reaction kinetics of selected fluoropolymer encapsulated sub-micron sized Al particles

Study on Preparation, Application and Modification of Flake Aluminium Powder