Abstract:Abstract Aluminum can enhance heat release of energetic composite in theory. However, the commonly used micron aluminum powder has several short comings like incomplete reaction and low reaction rate. Meanwhile, outer oxide shell of nano Al particle is thicker than micro Al, which leads to low active aluminum content and insufficient heat release. On the basis of previous research, reported fluoropolymers modified Al particles were compared and suitable F2311was chosen. Sub-micron scale Al (median particle size around 200 nm) was regarded as optimum coated object in consideration of activity content of aluminum powder changing with particle size. The super fine Al powder was prepared by electrical explosion method, and encapsulated in situ by selected fluorine rubber F2311. The experiments on thermal stability demonstrated F2311 coating thickness should be no less than 3.6 nm. These results were further confirmed by EXPLO5 thermo dynamic calculation. Calculated results showed that reaction characters of F2311 encapsulated Al exceeded conventional nano Al regardless of combustion and explosion. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), laser particle size analyzer and X-ray photoelectron spectroscopy (XPS) were used to characterize coated products’ morphology, particle size distribution and interfacial bonding information. The results showed that the coated samples were generally spherical shape, with median particle size of 217.7 nm and coating thickness of 3.6 nm. The coating shell contained a small amount of alumina and aluminum fluoride besides fluoropolymer. The non-isothermal dynamic equations of Al/F2311 and Al/Al 2 O 3 were deduced by TG/DSC simultaneous thermal analysis. Compared with conventional nano-Al, the apparent activation energy of Al/F2311 decreased by 45 kJ/mol and the first exothermic peak temperature was about 10 °C earlier. Moreover, heat release was nearly twice as conventional nano-Al. TG-DSC-MS coupled measurements certified that active Al was enveloped by ‘fluorine atmosphere’ while F2311 decomposed in range of 200–400 °C. Alumina was replaced with aluminum fluoride inside coating layer during 400–550 °C, which broadened the diffusion path and then accelerated the permeation of oxidizing gas. In addition, the exothermic of Al-F was obviously larger than Al-O. Consequently, the oxidation reaction was activated rapidly, especially in initial exothermic period. Fluoropolymer encapsulated sub-micron sized Al was a latent highly activity energetic fuel and a potential candidate for aluminum powder.

Ignition and Combustion Characteristics of Aluminum-Based Fluorine-Containing Composite Powder

Calcium Fluoride Promoting the Combustion of Aluminum Powder

The combustion-supporting mechanism of fluoropolymer on aluminum particles using reactive dynamics simulations

Combustion Mechanism of Fluorinated Organic Compound-Modified Nano-Aluminum Composite Particles: Towards Experimental and Theoretical Investigations

Micro-explosion-induced Combustion and Agglomeration Characteristics in Composite Propellants with Fluorinated Graphene

Sodium Fluoroaluminate Promoting the Combustion of Micron-Sized Aluminum Powder with Different Particle Sizes in Carbon Dioxide

In situ preparation of Al@3-Perfluorohexyl-1, 2-epoxypropane@glycidyl azide polymer (Al@PFHP@GAP) high-energy material

An approach to the induced reaction mechanism of the combustion of the nano-Al/PVDF composite particles

Enhanced combustion performance of core-shell aluminum with poly(vinylidene fluoride) interfacial layer: Constructing the combination bridge of aluminum powder and poly(vinylidene fluoride)

Potassium fluoride improving the ignition and combustion performance of micron-sized aluminum particles in high temperature water vapor

Core-shell particle of aluminum-copper perfluorooctanoate configurations and its ignition and combustion properties

Graphite fluoride as a new oxidizer to construct nano-Al based reactive material and its combustion performance

Combustion-supporting Effect of Boron Powder on Aluminum Powder

A latent highly activity energetic fuel: thermal stability and interfacial reaction kinetics of selected fluoropolymer encapsulated sub-micron sized Al particles

Preparation of anhydrous FeF 2 by solvothermal method and its application in composite energetic materials

Preparation of high-energy Al-Li alloy powders with enhanced compatibility and combustion performance by dense fluorosilane polymer composite coating

Enhancing the combustion of nAl with AlF 3 coating: gas–solid reaction mechanism for reducing combustion agglomeration of Al powder

Anti-sintering behavior and combustion process of aluminum nano particles coated with PTFE: A molecular dynamics study

Preparation and characterization of core-shell Al@PFHP with improving the combustion and ignition properties of aluminum powder

Rational design of gradient structured fluorocarbon/Al composites towards tunable combustion performance

Exploring the Combustion Mechanism of Single Micron-Sized Aluminum Particles with a Numerical Model