High-frequency localized surface plasmon polariton effects of Al nanoparticles on deep-blue BCzVBi OLEDs

Wang Yin-Xia,Bai Xiao-Chuan,Zhang Yong,Li Guo-Qing,

DOI: https://doi.org/10.7498/aps.73.20230858

IF: 0.906

2024-01-01

Acta Physica Sinica

Abstract:It is difficult to enhance the blue or purple luminescence efficiency of organic light-emitting devices (shortened as OLEDs) for practice display applications. In this article, aluminum nano particles (Al-NPs) were inserted into the light-tight TmPyPb electron transporting layer (ETL) of ITO/PEDOT:PSS/TAPC/BCzVBi:BCPO/TmPyPb/Liq/Al OLEDs, in which BCzVBi can emit deep-blue fluorescent lights, with the attempts to overcome the above deficiency through the local surface plasmon polariton(LSPP) effects excited in Al-NPs at more higher resonance frequencies by the luminescence radiations from BCzVBi. The distances of Al-NPs away from BCzVBi:BCPO fluorescent layer were chosen as x =4, 8, 12 nm. The morphology observation by atom force microscope and scan electron microscope showed that the Al film with thickness of 1 nm deposited at room temperature by vacuum heat evaporate is composed of separated Al grains (therefore, called as Al-NPs) with sizes at a 10 nm scale. Inserting these Al-NPs into the TmPyPb ETL, both the current density and luminance at the same voltage decreased relative to reference devices(ones without Al-NPs, namely) due to the worsened carrier mobility. However, the decreases of current density and luminance both got better at x =8 nm. This may be attributed to that the fluorescence quenching strongly occurs at x < 8 nm, and on the other hand, the local surface plasmon polariton over weakens at x > 8 nm due to attenuated radiations from BCzVBi. At x =8 nm, the voltage (9 V) to obtain maximum luminance was the same as that for the reference devices, but the maximum luminance itself deceased from 4200 Cd· m -2 to 3500 Cd· m -2 . However, the current density also decreased from 335.19 mA·cm -2 to 145.71 mA·cm -2 . This conversely resulted in a promising great increase of current efficiency from 0.88 Cd·A -1 to 2.36 Cd·A -1 . Subsequently, the external quantum efficiency(EQE) enhanced 170%, while the efficiency roll off ratio also reduced 61% with a decrease from 78% to 30.5%. At a high current density of 270 mA·cm -2 , EQE enhanced 66.5%. The coupling between fluorescence excitation state and local surface plasmon polariton is determined by the overlapping of fluorescence emitting peak and plasmon resonance peak. As aluminum has a number density of free electron (18.1×10 22 cm -3 ), much larger than that for the other normally used metals (such as gold and silver), its spectrum of local surface plasmon polariton can enough cover the fluorescence wavelength range of BCzVBi. These research results strongly imply that the luminescence efficiency of deep-blue OLEDs can be turn better by LSPP excited in Al-NPs at higher resonance frequencies.

physics, multidisciplinary