Abstract:The failure of composite laminates under cyclic fatigue loads is complex, as multiple failure mechanisms are in play at different scales and interact with each other. Predicting the remaining fatigue life as well as the residual capacities of a composite laminate or component is crucial, particularly for safety-critical applications. A progressive fatigue model is proposed to describe the catastrophic failure of open-hole laminates under tensile cyclic fatigue. To represent both intra-laminar and inter-laminar damage, a combination of a continuum damage mechanics model (CDM) and a discrete cohesive zone model (CZM) is implemented in the finite element (FE) software Abaqus. The CDM combines fibre- and matrix-dominated S-N curves with the Palmgren–Miner accumulation rule and Hashin’s residual strength to form a fatigue failure criterion differentiating between fibre failure (FF) and matrix failure (MF). The CZM implemented in this work is the CF20 model proposed by NASA. Fatigue cycling is simulated using an external cycle-jump scheme, where the stiffness degradation is conducted between the FE simulations outside of the implicit solver [90/0] s. Glass fibre reinforced polymer (GFRP) open-hole specimens were tested in tensile cyclic fatigue at a load ratio of 0.1. The experiments were reproduced numerically and the results compared. After calibration of a set of parameters based on one load level, the model was able to reproduce the experimental S-N curve very well, predicting a slope of −0.10, while the experimental value was −0.11. The failure sequence of the laminate was also successfully reproduced. The growth of the split from the hole, and its interaction with inter-laminar delamination, was successfully captured. The proposed approach was able to describe the fatigue failure of an open-hole laminate with a minimal set of material inputs using a simplified fatigue damage model while avoiding convergence issues.

Fatigue and Progressive Damage of Thin Woven CFRP Plates Weakened by Circular Holes

Failure Mechanism of Tensile CFRP Composite Plates with Variable Hole Diameter

Influence of the Fatigue Load Level and the Hole Diameter on the Laminate Structure’s Fatigue Performance

FE Analysis of Stress Concentrations in Composite Plates with Multiple Holes for Zigzag Multi-Fastened Joints

High-cycle random vibration fatigue behavior of CFRP composite thin plates

CFRP Thin-Ply Fibre Metal Laminates: Influences of Ply Thickness and Metal Layers on Open Hole Tension and Compression Properties

The fatigue performances of carbon fiber reinforced polymer composites- A review

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates

Computational Fatigue Life Analysis of Carbon Fiber Laminate

Fatigue Damage Behavior and Mechanism Research of 2198 Aluminum–Lithium Alloy Sheet with Error Holes

Tensile Behavior of Double-Hole CFRP Composite with Different Holes Position

Progressive fatigue damage modeling of laminated composites using strain-based failure criteria

Fatigue behaviour of cracked steel plates reinforced with uhm cfrp laminate

Fatigue performance of carbon fiber‐reinforced polymer strengthened single‐edge cracked steel plates: Effects of adhesive property and CFRP arrangement

Prediction of Long-term Fatigue Strength of Quasi-isotropic CFRP Laminates with a Hole under Compressive Loading

Damage evaluation in plain-woven CFRP plate with circular hole under cyclic tensile loading using electrical impedance tomography

Fatigue damage monitoring of composite laminates based on acoustic emission and digital image correlation techniques

Fatigue-driven failure criterion for progressive damage modelling and fatigue life prediction of composite structures

Characterization of early fatigue damage in CFRP unidirectional laminates based on Micro‐CT

Thermal plasticity deformation buckling analysis on the carbon fiber-reinforced aluminum matrix composite material

Fatigue Design of CFRP Strengthened Steel Members