Microstructural evolution and mechanical property of Al–Mg–Mn alloys with various solidification cooling rates
Yu Wang,Minqiang Gao,Bowei Yang,Ertuan Zhao,Fengguo Liu,Renguo Guan
DOI: https://doi.org/10.1016/j.matchar.2021.111709
IF: 4.537
2022-02-01
Materials Characterization
Abstract:In the present work, the microstructural evolution and mechanical property of as-cast Al–6 Mg–0.8Mn alloys with respect to the solidification cooling rate was investigated. The results demonstrate that as the cooling rate increases from 0.5 K/s to 46.9 K/s, the average grain size decreases firstly and then increases slightly; the average secondary dendrite arm spacing, the average length of Al6Mn and Al3Mg2 phases decreases. A high cooling rate (21.3 K/s and 46.9 K/s) causes the increase in the solute segregation/shrinkage porosities, and a low cooling rate (0.5 K/s) leads to the formation of casting defects, thus deteriorating the mechanical properties of alloys. The alloy with the cooling rate of 5.4 K/s shows an optimum mechanical property i.e., the tensile strength, yield strength, and elongation are 298.7 MPa, 133.8 MPa, and 30.5%, respectively. The enhanced strength-ductility synergy is mainly attributed to the refined secondary dendrite arm spacing and reduced casting defects. This work provides a reference for the fabrication of as-cast Al–Mg–Mn alloys with excellent mechanical performance.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing